C.H. Booth,F. Bridges,J. B. Boyce,T. Claeson
Abstract:We have performed fluorescence x-ray absorption fine-structure (XAFS) measurements from 20-200 K on a 5000 Å, c-axis film of YBa_2Cu_3O_{7-\delta} (YBCO) on MgO (Tc=89 K) using photons polarized perpendicular to the film. These data are compared to YBCO data from a single crystal and from a film on LaAlO_3 with the same Tc. The main difference between the single crystal and the film data is that while the single crystal data is well described by a two-site axial oxygen [O(4)] distribution, we see no evidence for such a distribution in either thin film sample. We place an upper limit on the size ofan axial oxygen splitting for the film on MgO at < 0.09 Å. Therefore, the magnitude of the splitting is not directly related to Tc. Fits to the temperature dependent data from the YBCO film on MgO indicate that all bonds show a smooth change of their broadening factor \sigma, except the Cu-O(4) bonds, which show an increase in \sigma in the vicinity of Tc, followed by a decrease of the same magnitude. Such a feature does not occur in diffraction measurements. Since XAFS measurements of \sigma include any correlation between the atoms in a given bond, we conclude that the O(4) position becomes less correlated with the Cu positions near Tc. Correlation measurements of these and several further near-neighbors are also reported.
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on the following aspects:
1. **Verification of oxygen position distribution**: The paper attempts to verify whether the distribution of oxygen positions (especially the axial oxygen O(4)) is consistent in YBa₂Cu₃O₇₋δ (YBCO for short), especially in thin - film and single - crystal samples. Previous studies have shown that in single - crystal YBCO, the O(4) position may be split (i.e., two different oxygen positions), but this result has not been fully confirmed in thin - film samples.
2. **Study of temperature dependence**: The paper also explores the behavior of these structural properties as a function of temperature, especially the changes near the superconducting transition temperature \(T_c\). Specifically, the researchers are concerned with how the width parameter \(\sigma\) of the Cu - O(4) bond changes with temperature and whether this change is related to the superconducting properties.
3. **Relationship between structure and superconductivity**: By comparing the data of single - crystal and thin - film samples, the paper aims to explore the relationship between structural properties (such as the splitting of the O(4) position) and superconducting properties. In particular, the researchers hope to determine whether the splitting of the O(4) position has a direct impact on the superconducting transition temperature \(T_c\).
### Main findings
- **Differences between single - crystal and thin - film**: The paper found that the O(4) position in single - crystal YBCO is indeed split, while no obvious splitting phenomenon was observed in thin - film samples. For single - crystal samples, the splitting of the O(4) position is about \(\Delta r\sim0.13\ Å\), while in thin - film samples, even at high temperatures, the splitting of the O(4) position is less than \(0.09\ Å\).
- **Temperature dependence**: For thin - film samples, the width parameters \(\sigma\) of all bonds change smoothly with temperature, except that the Cu - O(4) bond shows an increase followed by a decrease when approaching \(T_c\). This phenomenon was not observed in diffraction measurements, indicating that XAFS measurements can capture the changes in inter - atomic correlations.
- **Relationship between superconductivity and structure**: The research results show that the splitting of the O(4) position is not a key factor in determining the superconducting transition temperature \(T_c\). Because even in thin - film samples without obvious splitting, the superconducting properties still exist and are similar to those of single - crystal samples.
### Conclusion
Through detailed XAFS measurements and data analysis, the paper draws the following conclusions:
- The O(4) position in single - crystal YBCO is split, while there is no obvious splitting phenomenon in thin - film samples.
- The width parameter \(\sigma\) of the Cu - O(4) bond shows a special change when approaching the superconducting transition temperature \(T_c\), which may be related to the superconducting mechanism.
- The splitting of the O(4) position is not a key factor in determining the superconducting transition temperature \(T_c\), but a local structural feature of superconducting materials.
These findings are helpful for a more in - depth understanding of the relationship between superconducting properties and local structure in YBCO and provide important experimental basis for further research.