Abstract:Biochar adsorption has emerged as a favorable and environmentally friendly approach for removing metals such as chromium (Cr) from wastewater. However, the use of pristine biochar (PBC) is limited due to its finite adsorptive capacity, selectivity, and potential for secondary pollution. In this study, a novel bifunctionalized magnetic biochar (BMBC) was fabricated by incorporating cystamine as a ligand and glutaraldehyde as a crosslinker into alkali-treated magnetic biochar (MBC). This chemical modification introduced numerous amino groups and disulfide bonds onto the surfaces of BMBC. The biochar adsorbents’ surface morphologies, crystal structures, and texture properties were characterized using SEM, XRD, and N2 adsorption-desorption techniques. The specific surface area was determined using the BET method. Furthermore, the surface functional groups and elemental compositions before and after adsorption were analyzed using FTIR and XPS, respectively. The results demonstrated higher Cr(VI) removal efficacy of BMBC (100%) than MBC (72.37%) and PBC (61.42%). Optimal conditions for Cr(VI) removal were observed at a solution pH of 2, a temperature of 50 °C, a reaction time of around 1440 min, and an initial adsorbate concentration of 300 mg/L. The sorption process followed a chemical mechanism and was controlled by monolayer adsorption, with a maximum adsorption capacity of 66.10 mg/g at 50 °C and a pH of 2, as indicated by the larger fitting values of the pseudo–second-order and Langmuir models. The positive ∆Ho and ∆So values and negative ∆G0 values suggested a spontaneous and endothermic Cr(VI) adsorption process with high randomness at the solid/liquid interface. The removal of Cr(VI) was attributed to the reduction of Cr(VI) into Cr(III) facilitated by the introduced amino acids, sulfur, and Fe(II), electrostatic interaction between Cr(VI) in the solution and positive charges on the adsorbent surface, and complexation with functional groups. The presence of co-existing cations such as Cu(II), Cd(II), Mn(II), and K(I) had little effect on Cr(VI) removal efficiency. At the same time, the co-existence of anions of Cl−, NO3−, SO42−, and HPO42− resulted in a 7.58% decrease in the Cr(VI) removal rate. After five consecutive adsorption/desorption cycles, BMBC maintained a high Cr(VI) removal rate of 61.12%. Overall, this novel BMBC derived from rice straw shows great promise as a biosorbent for treating Cr(VI) in wastewater.

Enhanced Cr(VI) removal by biochar-loaded zero-valent iron coupled with weak magnetic field

Nano zero-valent iron loaded corn-straw biochar for efficient removal of hexavalent chromium: remediation performance and interfacial chemical behaviour

Sodium citrate and biochar synergistic improvement of nanoscale zero-valent iron composite for the removal of chromium (Ⅵ) in aqueous solutions

Removal of Aqueous Cr(VI) by Tea Stalk Biochar Supported Nanoscale Zero-Valent Iron: Performance and Mechanism

Removal/adsorption mechanisms of Cr(VI) and natural organic matter by nanoscale zero-valent iron-loaded biochar in their coexisting system

Efficient Removal of Cr(VI) from Aqueous Solution by Fe-Mn Oxide-Modified Biochar

Carbon matrix of biochar from biomass modeling components facilitates electron transfer from zero-valent iron to Cr(VI)

Integrated green complexing agent and biochar modified nano zero-valent iron for hexavalent chromium removal: A characterisation and performance study

Removal mechanisms of Cr(VI) and Cr(III) by biochar supported nanosized zero-valent iron: Synergy of adsorption, reduction and transformation

Ball milling biochar iron oxide composites for the removal of chromium (Cr(VI)) from water: Performance and mechanisms

Removal of Chromium (VI) by a Magnetic Nanoscale Zerovalent Iron–Assisted Chicken Manure-Derived Biochar: Adsorption Behavior and Synergetic Mechanism

Formation and mechanism of nanoscale zerovalent iron supported by phosphoric acid modified biochar for highly efficient removal of Cr(VI)

Nanoscale zero-valent iron particles supported on sludge-based biochar for the removal of chromium (VI) from aqueous system

Pyrolysis temperature and feedstock affected Cr(VI) removal capacity of sulfidated zerovalent iron: Importance of surface area and electrical conductivity

Removal of hexavalent chromium from aqueous solution by different surface-modified biochars: Acid washing, nanoscale zero-valent iron and ferric iron loading

One-pot synthesis of a magnetic Zn/iron-based sludge/biochar composite for aqueous Cr(VI) adsorption

Remediation of Cr(VI)-contaminated soil by ball milling modified zero-valent iron biochar composites: Insights into long-term stability and microbial community

Sodium citrate and biochar synergistic improvement of nanoscale zero-valent iron composite for the removal of chromium (VI) in aqueous solutions

The contribution of lignocellulosic constituents to Cr(VI) reduction capacity of biochar-supported zerovalent iron

Mechanism enhanced active biochar support magnetic nano zero-valent iron for efficient removal of Cr(VI) from simulated polluted water

Application of a Novel Bifunctionalized Magnetic Biochar to Remove Cr(VI) from Wastewater: Performance and Mechanism