Abstract:Designing cost-effective and high-stable heterostructures with synergistic active sites could simultaneously catalyze oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) for the (sea) water splitting. However, there are still challenges in maintaining the catalytic performance of individual materials and in constructing intimate interfaces. Herein, the novel corrosion engineering method is provided to prepare self-standing Fe 2 O 3 -Pt/NF nanoflowers where ultra-small amount of Pt combined with Fe 2 O 3 are in situ grown on the nickel foam (NF) in the corrosion system of "H 2 PtCl 6 -NaCl-FeCl 3 ". The synthesized Fe 2 O 3 -Pt/NF delivers the existence of Pt-O bond, which can regulate the electronic structure of active sites and optimize the binding energy of reaction intermediates, endowing the improvement of catalytic performance. Compared with Pt/NF and FeOOH/NF, the Fe 2 O 3 -Pt/NF heterostructure exhibits remarkable electrocatalytic activities with overpotentials reaching 94 mV and 265 mV for HER and OER, respectively, at a high current density of 100 mA cm −2 in alkaline solution. Furthermore, the self-assembled electrolytic cell employing Fe 2 O 3 -Pt/NF as the bifunctional electrode only requires the potential of 1.60 V and 1.61 V to achieve the current density of 100 mA cm -2 in overall water and seawater splitting, respectively. This material can be maintained for 10 hours of stable operation without obvious attenuation, indicating its good environmental adaptability and stability. Specifically, the enhanced catalytic activity and stability can be ascribed to the abundant active sites of nanoflowers, fast electron transfer rate of intimate interfaces, and strong electronic interaction between Pt atoms and Fe 2 O 3 . This work provides a new insight into the construction of highly efficient co-catalysts with intimate interfaces based on corrosion engineering methods.

In situ fabrication of sporoid-like flexible electrodes via Fe-regulated electron density for highly efficient and ultra-stable overall seawater splitting

Economical Iron-Based Catalyst Electrode for Highly Stable Catalytic Industrial-Scale Overall Seawater Splitting

Fabrication of ultra-stable and high-efficient CoP-based electrode toward seawater splitting at industrial-grade current density

3D self-supporting porous NiFe2O4-Ni3P-Fe2P film with sea urchin-like structure for efficient oxygen evolution

Scale-Up Preparation of Flexible Ni–W–P@Fiber Cloth Electrode for Boosting Overall Water Electrosplitting

Multiscale manipulating induced flexible heterogeneous V-NiFe2O4@Ni2P electrocatalyst for efficient and durable oxygen evolution reaction

Scalable Fabrication of Highly Active and Durable Membrane Electrodes Toward Water Oxidation.

Constructing self-standing Fe2O3-Pt/NF nanoflowers with synergistic active sites for efficient electrocatalytic overall (sea) water splitting

One-step electrodeposition synthesis of NiFePS on carbon cloth as self-supported electrodes for electrochemical overall water splitting

Fabrication of hierarchically structured S-doped NiFe hydroxide/oxide electrodes for solar-assisted oxygen evolution reaction in seawater splitting

Fabrication of Ultra‐Durable and Flexible NiPx‐Based Electrode toward High‐Efficient Alkaline Seawater Splitting at Industrial Grade Current Density

Interfacial Electronic Redistribution via Anionic Modulator for Superb and Highly Stable Water/Seawater Oxidation

Confined growth of Ultrathin, nanometer-sized FeOOH/CoP heterojunction nanosheet arrays as efficient self-supported electrode for oxygen evolution reaction

Engineering FeOOH/Ni(OH) 2 Heterostructures on Ni 3 S 2 Surface to Enhance Seawater Splitting

Multiscale Engineering of Nonprecious Metal Electrocatalyst for Realizing Ultrastable Seawater Splitting in Weakly Alkaline Solution

Mild Construction of "Midas Touch" Metal-Organic Framework-Based Catalytic Electrodes for Highly Efficient Overall Seawater Splitting

Ultrafast Room‐Temperature Synthesis of Large‐Scale, Low‐Cost, and Highly Active Ni─Fe Based Electrodes toward Industrialized Seawater Oxidation

Lattice-strained and ultra stable non-noble metal electrocatalysts for overall water splitting

Electrodeposition of NiFe-layered double hydroxide layer on sulfur-modified nickel molybdate nanorods for highly efficient seawater splitting

A low‐cost Ni‐Mo electrocatalyst for highly efficient hydrogen and oxygen evolution reaction

A Highly Efficient Fe-doped Ni3S2 Electrocatalyst for Overall Water Splitting