The optimization of hydrogel strength from cassava starch using oxidized sucrose as a crosslinking agent

Fitri Nur Kayati,Chandra Wahyu Purnomo,Yuni Kusumastuti,Rochmadi

DOI: https://doi.org/10.1515/gps-2023-0151

2023-01-01

Green Processing and Synthesis

Abstract:Abstract The mechanical properties of hydrogels are crucial in wound dressing application. Starch-based hydrogels have deficiencies in mechanical strength and gel stability. These shortcomings can be addressed by employing crosslinking techniques with oxidized sucrose. A design of experiments approach was used to optimize the tensile strength of the product. The results indicated that both the composition of oxidized sucrose and glycerol significantly impact tensile strength ( p -value < 0.05). The optimal tensile strength achieved was 27 MPa, using 0.9762 mL of oxidized sucrose and 0.0624 g of glycerol per gram of starch. The hydrogel products underwent a series of characterizations, including optical microscope examination, Fourier Transform Infrared Spectroscopy (FTIR), Proton Nuclear Magnetic Resonance ( 1 H NMR), swelling test, Water Vapor Transmission Rate (WVTR), contact angle, and cytotoxicity test. The FTIR and 1 H NMR analyses confirmed the crosslinking of hydroxyl groups within starch molecules with aldehyde groups from oxidized sucrose. Characterization of this hydrogel revealed that it had a swelling capacity of 95%, a WVTR of 714.92 g per m 2 per 24 h, a contact angle of 74.76°, and a cell viability value greater than 100%. Thus, this hydrogel is suitable for wound dressing due to its strength, exudate-absorbing capabilities, moisture retention properties, hydrophilicity, and non-toxicity.

engineering, chemical,green & sustainable science & technology,chemistry, multidisciplinary