Effect of Crack Blunting on Subsequent Crack Propagation

J. Schiøtz,A. E. Carlsson,L. M. Canel,Robb Thomson

DOI: https://doi.org/10.48550/arXiv.cond-mat/9512041

1995-12-07

Abstract:Theories of toughness of materials depend on an understanding of the characteristic instabilities of the crack tip, and their possible interactions. In this paper we examine the effect of dislocation emission on subsequent cleavage of a crack and on further dislocation emission. The work is an extension of the previously published Lattice Greens Function methodology. We have developed a Cavity Greens Function describing a blunt crack and used it to study the effect of crack blunting under a range of different force laws. As the crack is blunted, we find a small but noticeable increase in the crack loading needed to propagate the crack. This effect may be of importance in materials where a dislocation source near the crack tip in a brittle material causes the crack to absorb anti-shielding dislocations, and thus cause a blunting of the crack. It is obviously also relevant to cracks in more ductile materials where the crack itself may emit dislocations.

Condensed Matter,Materials Science

What problem does this paper attempt to address?

The problem this paper attempts to address is the impact of crack passivation on subsequent crack propagation. Specifically, the authors investigate the effect of dislocation emission at the crack tip on subsequent crack propagation and further dislocation emission. By extending the previous lattice Green's function method, the paper develops a cavity Green's function to describe passivated cracks and uses it to study the effects of crack passivation under different force laws.

### Main Research Content:
1. **Impact of Crack Passivation on Crack Propagation**: The study found that as the crack becomes passivated, a larger load is required to continue crack propagation. This effect is particularly important in brittle materials, where dislocations near the crack tip may be absorbed from nearby sources, leading to crack passivation.
2. **Impact of Crack Passivation on Dislocation Emission**: Passivated cracks are more likely to emit dislocations than sharp cracks. This is inherently significant in brittle materials, where sharp cracks naturally tend to propagate through cleavage rather than dislocation emission.
3. **Dislocation Emission Direction of Asymmetric Passivated Cracks**: The study also found that dislocation emission from asymmetric passivated cracks mainly occurs on one side, and this emission maintains the shape of the crack, leading to multiple dislocations being emitted to the same side, even when dislocation emission on two symmetric slip planes should be equivalent.

### Methods:
- **Molecular Dynamics Simulation**: Due to the very slow decay of the stress field, ordinary molecular dynamics simulations are very difficult. Therefore, the authors adopted an improved method, describing the elastic response of the surrounding medium through the Green's function. This method divides atoms into two categories: atoms near the crack tip interact through nonlinear forces, while atoms far from the crack tip interact through linear forces.
- **Calculation of Green's Function**: By calculating the Green's function, the total energy of the system can be effectively described, thereby reducing the use of computational resources.

### Conclusion:
- **Passivated Cracks are More Likely to Emit Dislocations**: Passivated cracks are more likely to emit dislocations than sharp cracks, which is inherently significant in brittle materials.
- **Directionality of Dislocation Emission**: Dislocation emission from asymmetric passivated cracks mainly occurs on one side, and this emission maintains the shape of the crack.

This study is of great significance for understanding the toughness and crack propagation mechanisms of materials, especially in brittle and plastic materials.