Facile hydrophilic modification of polydimethylsiloxane-based sponges for efficient oil–water separation

Chao-Jen Wang,Wei-Fan Kuan,Hui-Ping Lin,Yury A. Shchipunov,Li-Jen Chen

DOI: https://doi.org/10.1016/j.jiec.2021.01.015

IF: 6.76

2021-04-01

Journal of Industrial and Engineering Chemistry

Abstract:Hydrophilic PDMS-based sponge was successfully synthesized via sugar templates and PDMS-<em>b</em>-PEO block copolymer additives.The template loading controlled sponge porosity, absorption capacity, and separation performance.Separation efficiency greater than 99.9% for oil-water mixture was achieved in cycled filtration tests.Ring-like residual deposits are often observed after drying suspension droplets on surfaces, known as the coffee-ring effect. The edge of an evaporating drop with particles on a <em>hydrophobic surface</em> would shrink in the early stage of evaporation process, and the aggregation of particles at the drop edge would pin the droplet at its <em>particle pinning concentration.</em> The suspension droplet with <em>silica</em> particles of larger sizes would trigger the self-pinning at smaller pinning concentrations, an opposite trend to that of <em>polystyrene</em> particles. Also, the SEM images show different deposition patterns after evaporation of sessile/pendant droplets with silica/polystyrene particles. For bi-dispersed particle suspensions, the larger <em>silica</em> particles accumulate at the bottom of the deposits, while different sizes of <em>polystyrene</em> particles always well-mixed in the deposits due to the gravity effect on the particle sedimentation. The large density difference between silica (2.079 g/cm³) and water (0.998 g/cm³) would induce high sedimentation velocity. The particles of larger sizes exhibit higher sedimentation velocities. The Stokes' law and mass conservation model were further applied to evaluate the competitive relationship between the sedimentation and height-average radial (capillary flow) velocities, respectively, in a droplet with different sizes of silica/polystyrene particles.<span class="display"><span><ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1226086X21000290-fx1_lrg.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download high-res image (118KB)</span></span></a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1226086X21000290-fx1.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download full-size image</span></span></a></li></ol></span></span>

engineering, chemical,chemistry, multidisciplinary