Abstract:Nickel-copper-zinc (NiCuZn) ferrites with high permeability and low magnetic loss have high application potential in high-frequency electronics. In this work, NiCuZn ferrite samples with different Cu contents were prepared by a two-step sintering method. First, the optimal temperatures of the two-step sintering method (1025/925 °C) were confirmed, thereafter the influence of the Cu content on the crystal structure, microstructure, magnetic and dielectric properties of NiCuZn ferrite were studied in detail. Structural characterization showed that an increase in Cu content promoted grain growth and resulted in NiCuZn ferrites with a denser microstructure and decreased porosity. However, a second phase of CuO formed once the content of Cu (x value) reached 0.16. The magnetic hysteresis loops revealed that the saturation magnetization increased as x increased and the highest value of 57.3 emu/g was obtained at x = 0.14. The dielectric property measurement showed that increasing the Cu content could improve the dielectric constant and reduce the dielectric loss. The permeability measurements showed an increase in permeability with Cu content from x = 0.10 to x = 0.14 and a decrease when x = 0.16. Consequently, a NiCuZn ferrite with an appropriate microstructure and with high permeability (μ'=855), low magnetic loss (tanδμ = 0.02), and high saturation magnetization (57.3 emu/g) could be obtained at a Cu content of x = 0.14 and sintering temperatures of 1025/925 °C in the two-step sintering method. This NiCuZn ferrite provides new guidance for developing RF frequency multilayer inductors.

The regulation of high-frequency magnetic properties of NiZnCo ferrite for miniaturized antenna application

Magnetic and dielectric properties of Co–Zn nanoferrites for high-frequency miniaturized antennas

The preparation and performances of Co-Zn 18H hexagonal ferrite with an ultra-high magnetic resonance frequency and low-loss characteristics

Bi3+ doping-adjusted microstructure, magnetic, and dielectric properties of nickel zinc ferrite ceramics for high frequency LTCC antennas

Monodomain Nicuzn Ferrite With High Miniaturization Factor And Low Magnetic Loss At 200 Mhz For Antenna Miniaturization

Optimization of Ni0.95−xZnxCo0.05Fe1.90Mn0.02O4 Ceramics with Promising Magneto-Dielectric Properties for VHF Antenna Miniaturization

TiO2 Tailored Low Loss NiCuZn Ferrite Ceramics Having Equivalent Permeability and Permittivity for Miniaturized Antenna

High Permeability and Low Loss Easy-Plane Ferrites with Multi-Ions Doped for Miniaturized 5G Antennas

Miniaturized T-DMB antenna based on NiCuZn ferrie

Effect of Divalent Metal Ions Substitution on the Magnetic Properties of Ba3Co2-Me Fe24O41 (me = Zn2+, Ni2+) Hexagonal Ferrites

Low Loss Composite Ferrite With Almost Equal Values of Permeability and Permittivity for Antenna Applications

The preparation and high-frequency electromagnetic properties of Co80Ni20 alloy particles for potential antenna applications

Magnetic and dielectric properties of NiCuZn ferrite with optimized Cu content and sintered by a two-step process

Miniaturized Antennas and Planar Bandpass Filters with Self-Biased NiCo-Ferrite Films

Mn-Substituted Co2z Ferrite Ceramics with Impedance Matching for Ultra-High Frequency Miniaturization Antennas

Dispersion of LiZnTiBi Ferrite Particles into PMDS Film for Miniaturized Flexible Antenna Application

Monodomain Design and Permeability Study of High-Q-Factor NiCuZn Ferrites for Near-Field Communication Application

A Low Loss Niznco Ferrite, Prepared Using A Hydrothermal Method, For Antenna Applications

Low-temperature-sintering of Co2Z ferrite materials via Dy3+ ion doping for use in high-frequency applications

Low Loss Co(2)Z Hexaferrite with Matched Permeability and Permittivity in Hf and Vhf Bands

Co 2 Z Hexaferrites with Equivalent Permeability and Permittivity in UHF Band