Optimizing Spectral Properties of Cesium Tungsten Bronze Films Doped with Silver Nanowires Based on the Machine Learning Method
Zeming He,Wenxi Xie,Siyang Zhang,Yin Gao,Ashraf Y. Elnaggar,Juanna Ren,Islam H. El Azab,Zeinhom M. El-Bahy,Ming Yang,Hang Zhang,Zhanhu Guo
DOI: https://doi.org/10.1021/acs.jpcc.4c03634
2024-01-01
Abstract:Glass exhibits high transmittance in the solar radiation band but high absorbance in the mid-far infrared (MIR) band, which causes a poor energy-saving effect. Thermal insulation coatings offer the most effective solution to address this. Among these, nano-cesium tungsten bronze (CsxWO3) had a strong blocking effect in the solar radiation band due to its intrinsic absorption, local surface plasmon resonance, and small polaron absorption, but its reflectivity in the MIR band was very low. Conversely, silver nanowires (AgNWs) formed a dense network structure with low transmittance and high reflectance in the MIR band; however, when mixed into Cs0.32WO3 slurries, the solar radiation-blocking ability was weakened. In order to assess the impact of AgNWs on the properties of Cs0.32WO3 films, this study collected experimental data from different Cs0.32WO3 films doped with AgNWs for multilayer perceptron (MLP) neural network machine learning. The trained models exhibited efficient and accurate prediction abilities. A large number of extrapolated independent variables were input to the trained MLP models using the grid search method, and then the predicted results of dependent variables were displayed in three-dimensional (3D) models to more intuitively show the influence of doping AgNWs on the optical performance of different Cs0.32WO3 films. Through an optimization analysis of two 3D models of T-550 nm (transmittance at 550 nm) and SC (shading coefficient), two transition values of T-550 nm were found: 69.5 and 64.2%. When T-550 nm surpassed 69.5%, the SC value of nondoped Cs0.32WO3 films was the lowest. Conversely, when T-550 (nm) was below 69.5%, doping with AgNWs decreased the SC value of Cs0.32WO3 films. Using the optimal mixture of Cs0.32WO3 slurries and AgNW slurry at a ratio of 1:3, the SC value of nondoped Cs0.32WO3 films was lower when T-550 (nm) exceeded 64.2%. Conversely, when T(550 nm)was below 64.2%, the same mixture resulted in a lower SC value. These predicted results and their accuracy were verified by experiments and provided important technical guidance and method support for future research and the application of high-performance Cs0.32WO3 films.