Abstract:The numerous industrial application of mild steel despite its susceptibility to degradation on exposure to the environment has called for the continuous search for materials that can protect its surface from contaminants which could affect its inherent properties. This paper therefore examined the corrosion-resistance, hardness, and microstructure properties of unripe plantain peel (UPP) nanoparticle-reinforced Zn–ZnO–MgO composite coatings deposited on the surface of mild steel (AISI 1015 Carbon Steel). The corrosion properties of the coated steel samples were investigated using the potentiodynamic polarization technique, utilizing simulated seawater (3.65% NaCl solution) as the test medium. The hardness of the coated steel samples was studied using the Brinell hardness method, while the microstructure properties were investigated using XRD and SEM/EDS. The as-received mild steel sample was observed to exhibit a hardness value and corrosion rate of 136.8 kgf/mm 2 and 8.6272 mm/year, respectively, while the Zn–10ZnO–10MgO-coated mild steel sample exhibited a hardness value and corrosion rate of 246.53 and 1.7698 mm/year, respectively. Relative to the other samples, the Zn–10ZnO–10MgO–6UPP-coated mild steel (sample coated with 10 g/L of ZnO, 10 g/L of MgO and 6 g/L of UPP) exhibited a highest hardness value and lowest corrosion rate of 254.77 kgf/mm 2 and 0.6645 mm/year, respectively. These corrosion rate and hardness values of the Zn–10ZnO–10MgO–6UPP-coated mild steel sample showed that the unripe plantain peel nanoparticles further enhanced the strengthening and passivating ability of Zn–ZnO–MgO–UPP coating. The SEM micrographs revealed that the Zn–ZnO–MgO–UPP coating possessed a more refined microstructure relative to the Zn–ZnO–MgO coating, signifying the grain refining ability of the unripe plantain peel nanoparticles. The EDS additionally indicated the occurrence of crucial and dispersion strengthening elements in the coatings. The XRD profile of the coatings exhibited high intensities, which signified that the coatings have high stability and good texture with microstructural and chemical homogeneity.

Development of starch-modified titanium oxide paired with zinc powder using the electrodeposition technique as a composite superhydrophobic coating for mild steel

Constructing Superhydrophobic WO3@TiO2 Nanoflake Surface Beyond Amorphous Alloy Against Electrochemical Corrosion on Iron Steel

Unveiling the anti-corrosion properties of Zn-eggshell particle composite coatings on mild steel in seawater-simulated solution using starch as a modifier

Corrosion Behavior of Al2O3-40TiO2 Coating Deposited on 20MnNiMo Steel via Atmospheric Plasma Spraying in Hydrogen Sulfide Seawater Stress Environments

Robust Superhydrophobic SiO2/polydimethylsiloxane Films Coated on Mild Steel for Corrosion Protection

Study on the corrosion resistance of KH570 modified titanium oxide coating synthesized at low temperature on 304 stainless steel

Superhydrophobic and corrosion-resistant of 2-methylimidazolezincsalt-based coating enhanced with silane modification

Development of UPP nanoparticles reinforced Zn–ZnO–MgO composite coating for corrosion-resistance, hardness, and microstructure property enhancement of AISI 1015 carbon steel for automotive and marine applications

Liquid Phase Deposited TiO2 Films on Stainless Steel Mesh for Corrosion Resistance Application

A Superhydrophobic Coating On Titanium Alloys By Simple Chemical Etching

Nano-micro structured superhydrophobic zinc coating on steel for prevention of corrosion and ice adhesion

Bifunctional TiO2/AlZr Thin Films on Steel Substrate Combining Corrosion Resistance and Photocatalytic Properties

Preparation of Different Coatings on 316 L Stainless Steel and their Corrosion Performance in Supercritical Water

Preparation of anti-corrosion superhydrophobic coatings by an Fe-based micro/nano composite electro-brush plating and blackening process

Preparation of Superhydrophobic Materials and Establishment of Anticorrosive Coatings on the Tinplate Substrate by Alkylation of Graphene Oxide

Facile Fabrication of TiN Coatings to Enhance the Corrosion Resistance of Stainless Steel

Da/Tio2 Composite Superhydrophobic Coatings with Enhanced Wear Resistance and Oil/Water Separation

Efficient one-step fabrication of superhydrophobic nano-TiO2/TMPSi ceramic composite coating with enhanced corrosion resistance on 316L

The long-term degradation behavior of the durable superhydrophobic coating on Al matrix

Comparative Study on Corrosion Characteristics of Al2O3/316L and TiO2/316L Stainless Steel in Supercritical Water

Corrosion of Ti Coating Prepared by Modified HVOF Process