Exploring Ce3+ adsorption on clay minerals to propel the frontier of heavy metal sensing with clay-CeO2 modified carbon paste electrode
Sondos Sadek,Abderrazek El-Kordy,Abdelrahman K. A. Khalil,Tahar Laoui,Abdel-Nasser Kawde,Abdelaziz Elgamouz
DOI: https://doi.org/10.1007/s10800-024-02125-9
IF: 2.925
2024-05-08
Journal of Applied Electrochemistry
Abstract:A novel approach was employed to craft innovative carbon-paste electrodes using cerium(IV) oxide (CeO 2 )-doped clay, aiming to modify graphite electrodes. The introduction of Ce involved the adsorption of Ce 3+ ions onto an activated carbon (AC) clay mixture, showcasing an impressive adsorption capacity of 40.0 mg g −1 , which surpasses that of clay alone. This step was undertaken to enhance the conductivity of raw clay and increase its electrochemical surface area. Sintering clay-CeO 2 at 1000 °C resulted in the maximum electrochemical area when utilized as a 10 wt% dopant for graphite electrodes. Heavy metal ion analysis (HMI) involving Cd 2+ , Pb 2+ , Cu 2+ , and Hg 2+ was conducted using five electrochemical techniques: Cyclic Voltammetry (CV), Square Wave Voltammetry (SWV), Normal Pulse Voltammetry (NPV), Differential Pulse Voltammetry (DPV), and Linear Sweep Voltammetry (LSV). SWV emerged as the optimal technique and was termed SWAdSV after the stripping process, displaying peak current responses for Cd 2+ (74.7 μA), Pb 2+ (42.4 μA), Cu 2+ (36.0 μA), and Hg 2+ (22.8 μA). Calibration curves were utilized to determine the Limit of Detection (LOD) and Limit of Quantification (LOQ) values for Cd 2+ , Pb 2+ , Cu 2+ , and Hg 2+ . The repeatability, expressed as %RSD, for the same electrode was found to be 1.70%, 2.04%, 1.14%, and 3.61% for Cd 2+ , Pb 2+ , Cu 2+ , and Hg 2+ . While the reproducibility, also expressed as %RSD, for different electrodes was determined to be 1.98%, 2.31%, 1.52%, and 1.89% for Cd 2+ , Pb 2+ , Cu 2+ , and Hg 2+ , respectively.
electrochemistry