Abstract:The design of Au-based materials with good dispersion and more active sites is critical to enhance the catalytic performance of electrochemical ammonia production. Herein, two-dimensional (2D) heterojunction Au-Bi2Te3 nanosheets (Au-Bi2Te3 NSs) are prepared by Au nanoparticles growing on Bi2Te3 nanosheets. Benefiting from the good dispersion of Au nanoparticles and the synergistic effect of the heterojunction composite, Au-Bi2Te3 NSs demonstrate excellent behavior for an ambient nitrogen reduction reaction (NRR). In a 0.1 M Na2SO4 electrolyte (N2-saturated), Au-Bi2Te3 NSs display a high NH3 yield rate of 32.73 μg h–1 mgcat.–1 and a faradic efficiency of 20.39% at −0.4 V. The proposed synthetic method provides a feasible strategy for designing high-performance heterojunction electrocatalysts for electrochemical ammonia synthesis.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c11246.Experimental details; SEM image; TEM images; AFM image; schematic illustration of the electrocatalytic NRR; calibration curve of N2H4, KNO3, and NH3; NH3 yields and FEs of different catalysts; concentration of N2H4·H2O and NO3–; UV–vis absorption spectra; XRD pattern; XPS spectra; energy-dispersive X-ray spectroscopy (EDX); elemental mapping images; cyclic voltammetry curves; EIS; atomic ratio (Table S1); particle size (nm) (Table S2); and more comparative information (Table S3) (PDF)This article has not yet been cited by other publications.

Low-overpotential electrochemical ammonia synthesis using BiOCl-modified 2D titanium carbide MXene

Efficient Electrocatalytic N2 Fixation with MXene under Ambient Conditions

Novel confinement of Mn3O4 nanoparticles on two-dimensional carbide enabling high-performance electrochemical synthesis of ammonia under ambient conditions

Au Sub-Nanoclusters on TiO 2 toward Highly Efficient and Selective Electrocatalyst for N 2 Conversion to NH 3 at Ambient Conditions.

High-Performance Electrocatalytic Conversion of N-2 to NH3 Using Oxygen-Vacancy-Rich TiO2 in Situ Grown on Ti3C2Tx MXene

An MnO2-Ti3C2Tx MXene Nanohybrid: an Efficient and Durable Electrocatalyst Toward Artificial N-2 Fixation to NH3 under Ambient Conditions

Bimetallic NiCo boride nanoparticles confined in a MXene network enable efficient ambient ammonia electrosynthesis

Ti3C2Tx (T = F, OH) MXene nanosheets: conductive 2D catalysts for ambient electrohydrogenation of N2 to NH3

Enhancing Electrocatalytic Ammonia Synthesis through Theoretical Design of Cluster Catalysts Supported on TiO 2 Surface

High-Efficiency Electrosynthesis of Ammonia with Selective Reduction of Nitrate in Neutral Media Enabled by Self-Supported Mn2CoO4 Nanoarray

Bioinspired Electrocatalyst for Electrochemical Reduction of N2 to NH3 in Ambient Conditions.

Two-Dimensional Heterojunction Electrocatalyst: Au-Bi 2 Te 3 Nanosheets for Electrochemical Ammonia Synthesis

Mn 3 O 4 Nanocube: An Efficient Electrocatalyst Toward Artificial N 2 Fixation to NH 3 .

Ti3c2tx ( T 1/4 F, Oh) Mxene Nanosheets: Conductive 2d Catalysts For Ambient Electrohydrogenation Of N2 To Nh3+

Electrocatalytic ammonia synthesis on Fe@MXene catalyst as cathode of intermediate-temperature proton-conducting solid oxide cell

Amorphous Boron Carbide on Titanium Dioxide Nanobelt Arrays for High‐Efficiency Electrocatalytic NO Reduction to NH3

A Simple Synthesis Of Co3o4@Cnt To Boost Electrochemical Nitrogen Fixation

High-Efficiency Electrosynthesis of Ammonia with Selective Reduction of Nitrate in Neutral Media Enabled by Self-Supported Mn 2 CoO 4 Nanoarray

High-efficiency electrocatalytic nitrite-to-ammonia conversion on molybdenum doped cobalt oxide nanoarray at ambient conditions

Atomically Dispersed Cu Sites on Dual‐Mesoporous N‐Doped Carbon for Efficient Ammonia Electrosynthesis from Nitrate

Two-Dimensional Mosaic Bismuth Nanosheets for Highly Selective Ambient Electrocatalytic Nitrogen Reduction