Improving cell proliferation using polylactic acid, polycaprolactone, hydroxyapatite and zinc oxide nanocomposite for cancellous bone substitutes

Farnaz Dehghani Firoozabadi,Ahmad Ramazani Saadatabadi,Azadeh Asefnejad
DOI: https://doi.org/10.1080/25740881.2023.2276775
2023-11-18
Polymer-Plastics Technology and Materials
Abstract:Different types of implants are used in orthopedic applications. Due to the stress shielding and a second surgery caused by applying metal implants as orthopedic joints, using biodegradable bone implants with antibacterial properties is advantageous. Therefore, this study aims at fabricating a multifunctional poly (lactic acid) (PLA)-polycaprolactone (PCL)-based scaffold reinforced with hydroxyapatite (HA) and zinc oxide (ZnO) nanoparticles. Solvent casting combined with die-casting techniques was employed for fabricating the scaffolds, and their physical, mechanical, and biological properties were characterized. The morphology of the samples and the growth of hydroxyapatite crystals on the surface of the samples were examined by field emission scanning electron microscope. In dry conditions, adding nanoparticles to the scaffolds has significantly ( p < .05) increased the tensile Young's modulus from 450.00 ± 87.18 MPa to 1050.66 ± 104.05 MPa. Also, adding ZnO has improved the antibacterial properties of the scaffolds against S.aureus and E.coli bacteria strains. Moreover, the MTT assay results (after 72 h cell culture) show that the viability of L929 cells has increased from 22.18 ± 0.62% for the PLA-PCL scaffold to 70.03 ± 0.25% for the optimal nanostructure ( p < .05). In conclusion, the PCL-PLA/HA/1% ZnO scaffold could potentially be used as absorbable spongy bone implants.
polymer science
What problem does this paper attempt to address?