Heteroatoms preintercalated Cl-terminated Ti3C2Tx MXene wrapped with Mesoporous Fe2O3 Nanospheres for improved Sodium ion Storage

Yishao Liu,Chenyu Gao,Ruxuan Zhou,Feng Hong,Guoqing Tong,Li Wang,Yang Jiang

DOI: https://doi.org/10.1039/d2nj05061g

IF: 3.3

2022-11-25

New Journal of Chemistry

Abstract:Developing multicomponent hybrid materials is an effective method to achieve structural stable anode materials for high-performance sodium-ion batteries (SIBs). In this work, mesoporous Fe2O3 nanospheres wrapped by heteroatoms pre-intercalated Cl-terminated Ti3C2Tx MXene as SIB anode materials are designed. The Cl-terminated Ti3C2Tx MXene is obtained by Lewis acidic etching route, which offers a green and practicable route to etching MAX precursors without HF. The MXene framework is pretreated by Borohydride and thus turns into a 3D structure to better support Fe2O3 nanospheres. In order to obtain Fe2O3@Ti3C2Tx anode, Fe2O3 nanospheres are distributed on Ti3C2Tx MXene framework by virtue of surfactant CTAB. Benefiting from the synergic effect of Fe2O3 nanospheres and heteroatoms-doped MXene framework, which can decrease Na ion diffusion barrier, this unique structure provides abundant ionic transfer paths and active sites to accelerate the electrochemical process. Furthermore, the volume change of Fe2O3 nanospheres can be effectively alleviated during the sodiation/desodiation process. Herein, the resultant Fe2O3@Ti3C2Tx anode has excellent sodium storage performance, high reversible capacity (350 mA h g−1 at 1.0 A g−1 after 200 cycles), considerable long-cycle stability (262.8 mA h g−1 at 2.0 A g−1 after 800 cycles) and calculated b values of the cathodic and anodic peaks are 0.89 and 0.94 respectively. All these analyses boost the commercial process of Fe2O3@MXene hybrids in SIBs.

chemistry, multidisciplinary