Sulfate Ion Diffusion Test of Recycled Aggregate Concrete with Different Replacement Ratio
Kai ZHANG,Liang-liang CHEN,Ke-bin SHI,Jing-wei GONG,Fu-fei WU
DOI: https://doi.org/10.3969/j.issn.1671-1815.2016.31.053
2016-01-01
Abstract:Recycled aggregate concrete can be a good solution to the problem of excessive urban construction waste and lack of aggregate resources .Durability is very important for the application of recycled aggregate concrete in practical engineering ,concrete is often subjected to sulfate attack to durability .Through respectively putting 0%, 50%, 30%, 70%, 90%replacement rate of recycled aggregate concrete was put into 5%sodium sulfate solution for corrosion of 2,4,6,8,10,12 months,stratified sampling of the sample was performed on each erosion cycle , through using EDTA complex titration method to test sulfate ion that erode for 12 months.The diffusion law of sulfate ion can be listed as follow:The sulfate content of 0%replacement rate of recycled aggregate concrete is increased from 0.43%to 2.24%, and the erosion depth is 21 mm.The sulfate content of 30%replacement rate of recycled aggregate concrete is increased from 0.54% to 2.66%, and the erosion depth is 21 mm.The sulfate content of 50%replacement rate of recycled aggregate concrete is increased from 0.61%to 3.40%, and the erosion depth is 24 mm.The sulfate content of 70% replacement rate of recycled aggregate concrete is increased from 0.70% to 3.98%, and the erosion depth is 27 mm.The sulfate content of 100%replacement rate of recycled aggregate con-crete is increased from 0.85%to 5.02%, and the erosion depth is 30 mm.In terms of 0%replacement rate of re-cycled aggregate concrete as the base erosion after 12 months of sulfate content and erosion depth ,50%, 30%, 70%, 100% replacement rate of recycled aggregate concrete sulfate content increased respectively by 17.13%, 54.14%, 81.22%, 130.39%.0%, 50%, 70%, 100% replacement rate of recycled aggregate concrete erosion depth increased respectively by 0%,14.29%, 28.57%,42.86%.And combined with the experimental results , the mechanism of the effect of different substitution rates on the diffusion of sulfate ion in recycled aggregate con-crete is analyzed in detail .It provides a reference for the application of recycled aggregate concrete in practical engi-neering .