Factors affecting microscopic basicity of silicate glasses from the perspective of O1s binding energy

Masahiro Tsuji,Masahiro Hotta,Takashi Watanabe,Rie Endo,Masahiro Susa,Miyuki Hayashi

DOI: https://doi.org/10.1002/srin.202300383

IF: 2.1258

2023-11-02

steel research international

Abstract:The factor affecting the microscopic basicity of oxygen in the Si–O–Si bond has been investigated on the basis of the O1s binding energy measured by X‐ray photoelectron spectroscopy (XPS). The samples used were SiO2, Na2O‐SiO2, CaO‐SiO2, CaO‐MgO‐SiO2 and CaO‐Al2O3‐SiO2. For analysis on clean surfaces, samples were finally prepared by fracturing in vacuum in an XPS system. From the O1s spectra, derived were the centers of gravity of the O1s spectra and the binding energies of O1s in the Si‐O‐Si, Si‐O‐Al, Al‐O‐Al, Si‐O‐Na, Si‐O‐Ca and Si‐O‐Mg bonds. A good linear relationship was found between the center of gravity of the O1s spectra and the optical basicity, suggesting that the center of gravity of the O1s spectra is a reasonable basicity index of silicate glasses used in this work. It was also found that there was a linear relationship between the binding energy of O1s in the Si–O–Si bond and the optical basicity, irrespective of the glass systems. This indicates that the experimental microscopic basicity of oxygen in Si–O–Si bond is affected not only by the first neighboring ions of oxygen, but also by the composition of the sample. This article is protected by copyright. All rights reserved.

metallurgy & metallurgical engineering