Fiber reinforcement of polymer hybrid sandwich composites using SNiPs: effect of silica nanoparticles on flexural and compressive strength
Megavannan Mani Thiyagu Murugaiyan Pradeep Kumar Krishnan a Institute of Mechanical Engineering,Saveetha School of Engineering,Saveetha Institute of Medical and Technical Sciences,Saveetha University,Chennai,Indiab Department of Mechanical and Industrial Engineering,College of Engineering,National University of Science and Technology,Al Hail,Sultanate of Oman
DOI: https://doi.org/10.1080/00405000.2024.2384103
IF: 1.7698
2024-07-25
Journal of the Textile Institute
Abstract:The increasing demand for lightweight, high-strength composite materials in aerospace, automotive, and structural applications has intensified research into polymer composites. To address the challenge of enhancing mechanical properties while maintaining weight efficiency, this study investigates the effect of silica nanoparticles (SNiPs) on the flexural and compressive strength of sandwich composites. These composites are constructed from fiber-reinforced carbon, para-aramid, glass, and polyurethane (PU) foam. Composite specimens with varying concentrations of SNiPs were produced using a hand layup process with synthetic fiber-reinforced polymer glass fibers (GFRP), carbon fibers (CFRP), para-aramid fibers (KFRP), urethane foam, and epoxy glue. Fabricated using a quasi-static stacking sequence technique, the composites feature a three-layer sandwich matrix(0 K 1 / 45° C 1 / 45° G 1 /PU/ 45° G 1 / 45° C 1 /0 K 1 ). Flexural and compressive strength tests were conducted to assess their mechanical behavior. The results show that incorporating SNiPs into polymer hybrid sandwich composites significantly enhances both flexural and compressive strength. This improvement is attributed to the high aspect ratio and surface properties of SNiPs, which facilitate effective stress transfer between the reinforcing fibers and the polymer matrix. The flexural strengths achieved with 0, 2, 4, and 6 wt.% SNiPs were measured as 52.583, 58.713, 64.108, and 61.397 MPa, respectively. Similarly, the compressive strengths were measured as 2.207, 2.813, 3.528, and 3.182 MPa for the respective weight percentages. This study examines the use of silica nanoparticles (SNiPs) for fiber reinforcement in polymer hybrid sandwich composites, aiming to enhance their mechanical properties.
materials science, textiles