High-performance wide-bandgap perovskite solar cells with enhanced photon-to-electron response of near-infrared wavelengths

Zhihai Liu,Lei Wang,Xiaoyin Xie,Chongyang Xu,Chao Zhang,Ping Chen

DOI: https://doi.org/10.1039/d3tc03458e

IF: 6.4

2023-10-21

Journal of Materials Chemistry C

Abstract:Wide-bandgap perovskite solar cells (PSCs) have been intensively investigated owing to their strong light absorption of short wavelengths and high open-circuit voltage. In this study, we improved the performance of wide-bandgap (1.74 eV) PSCs by incorporating a non-fullerene acceptor of Y6 into the Cs0.12MA0.05FA0.83Pb(I0.6Br0.4)3 perovskite film, which could enhance the photon-to-electron response at near-infrared wavelengths. Due to the Lewis-base groups, inserting Y6 could effectively passivate the vacancy-induced defects in the perovskite film, which further facilitated the charge transport of the PSCs. As a result, power-conversion-efficiency (PCE) of the wide-bandgap PSCs was significantly improved from 17.6% to 19.8% (on average), which was mainly induced by the conspicuously enlarged short-circuit current density. With the introduction of Y6, long-term stability of the PSCs (without encapsulation) was simultaneously enhanced with the PCE degradation significantly suppressed from 33.5% to 16.7% after a measurement of 15 days. The best PSC with Y6 exhibited a highest PCE of 20.2%, with a stable power output and negligible hysteresis. Our results demonstrate the superior effect of Y6 on boosting the performance of wide-bandgap PSCs.

materials science, multidisciplinary,physics, applied