An In Vitro Study of the Effect of Aluminum and the Combined Effect of Strontium, Aluminum, and Fluoride Elements on Early Enamel Carious Lesions
Haroula Koletsi-Kounari,Eleni Mamai-Homata,Iliana Diamanti
DOI: https://doi.org/10.1007/s12011-012-9328-6
IF: 4.081
2012-01-28
Biological Trace Element Research
Abstract:The purpose of this in vitro study was to evaluate the effect of aluminum and of combined strontium, aluminum, and fluoride treatments on enamel demineralization and remineralization. During a 6-day pH-cycling protocol, pre-softened bovine enamel slabs were immersed twice daily for 1 min in the following experimental solutions: (a) distilled water [W] (negative control); (b) 1,000 ppm F [F] (positive control); (c) 1,000 ppm Al [Al]; (d) 1,000 ppm Al, 1,000 ppm F applied interchangeably [Al–F]; (e) 1,000 ppm Al, 1,000 ppm F, applied in sequential order [Al + F]; (f) combined 1,000 ppm Al and 150 ppm Sr [Al + Sr]; and (g) combined 150 ppm Sr and 1,000 ppm F [Sr + F]. Subsequently, the specimens were subjected to a 5-day acid resistance test. Lesions were evaluated quantitatively by performing surface microhardness and qualitatively by using polarized light microscopy. According to the results, solutions [Sr + F] and [Al–F] enhanced remineralization and inhibited demineralization as effectively as the [F] solution and significantly superiorly compared to [Al + Sr] and [Al] solutions. All tested solution groups, except for the [Al + Sr] group, presented significantly increased resistance to acidic attack, compared to [W]. PLM examination revealed that all solution groups, except for the [W] group, developed an acid-resistant zone at lesion surfaces. In conclusion, under the present experimental conditions, the combined strontium–fluoride and aluminum–fluoride treatments presented similar anti-caries efficacy compared to fluoride treatment alone, but they did not show evidence of synergistic activity on pre-softened enamel.
biochemistry & molecular biology,endocrinology & metabolism