Reactive Diluent Derived from Ferulic Acid for the Preparation of a Fully Biobased Unsaturated Polyester Resin
ZengHui Dai,Qing Li,ZhiWei Chen,Rashidul Kabir Shawon,YiYuan Zhu,HongFen Lv,FeiYa Fu,YaoFeng Zhu,YaQin Fu,XiangDong Liu
DOI: https://doi.org/10.1021/acssuschemeng.0c05187
2020-11-18
Abstract:A reactive diluent for the preparation of a fully biobased unsaturated polyester resin (UPR) was developed and is presented here. The diluent, 4-vinylguaiacol acetyl ester (AC4VG), was obtained via a simple two-step synthesis: decarboxylation from ferulic acid (FA) and acetylation of the decarboxylated product, 4-vinylguaiacol (4VG). This diluent shows excellent miscibility with biobased unsaturated polyester prepolymer (UPP) that had been synthesized from succinic acid (SA), 1,3-dihydroxypropane (PD), and itaconic acid (IA). A mixed solution of these possessed a very low viscosity at 174 mPa·s at room temperature when 40 wt% AC4VG was added. Moreover, its vinyl group brought high reactivity for free radical copolymerization with the UPP, and the benzene ring structure enabled a high glass transition temperature (Tg) of the cured UPR. When the fully biobased UPR was reinforced by cotton fabric, a strong tensile strength at the break of approximately 65.8 MPa, a Tg of 135 °C, and a Td5% of 276 °C were achieved. This work suggests that the fully biobased UPR reported here is a promising candidate for replacing petroleum-based ones, and the diluent AC4VG played an important role in the performance of this biobased UPR.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.0c05187.The 1H NMR and FTIR spectra of FA, 4VG, AC4VG, and the UPPs, mechanical, thermal, and thermodynamic properties of the UPCom composites (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology