Mechanochemical synthesis of graphitic carbon nitride/graphene oxide nanocomposites for dye sorption

Aniruddha Molla,Ji Ho Youk

DOI: https://doi.org/10.1016/j.dyepig.2023.111725

IF: 5.122

2023-09-27

Dyes and Pigments

Abstract:The nanocomposites of graphitic carbon nitride supported on graphene oxide (g-C 3 N 4 /GO) were synthesized using the mechanochemical method, effectively leveraging the synergistic benefits of mechanical energy and chemical reactions. The sorption performance of g-C 3 N 4 /GO for methylene blue (MB) was explored using the Langmuir adsorption isotherm. The g-C 3 N 4 /GO nanocomposite exhibited a maximum sorption capacity (q max ) value of 116.41 ± 5.46 mg g −1 for MB at pH 7, while GO and g-C 3 N 4 displayed q max values of 55.71 ± 3.11 and 17.01 ± 1.65 mg g −1 , respectively. The superior q max value of g-C 3 N 4 /GO was attributed to the mechanochemical exfoliation of both GO and g-C 3 N 4 , resulting in its increased surface area and favorable surface characteristics. The highest sorption of MB on g-C 3 N 4 /GO was achieved at pH 10, with the q max value of 191.20 ± 9.94 mg g −1 . Furthermore, g-C 3 N 4 /GO demonstrated good reusability, maintaining a removal efficiency of 92% after five consecutive sorption cycles of MB. The sorption process was spontaneous at all the tested temperatures. A positive ΔH 0 value of 18.8 kJ mol −1 suggests that the sorption process is predominantly physisorption. In the case of the negatively charged methyl orange (MO), no sorption occurred on the g-C 3 N 4 /GO. A red shift of 22 nm in the λ max of MO was instead observed due to the protonation of the azo group.

engineering, chemical,chemistry, applied,materials science, textiles