Comprehensively understanding the distinct properties of crystal structure, phase transition and dielectrics in [M(crown)n]ReO4 (M+ = Na+, K+, NH4+; crown = 15-crown-5, 18-crown-6; n = 1 or 2)
Guo-Jun Yuan,Xue-Wei Pan,Yan Gao,You-Fang Jiang,Li Li,Xiaoming Ren
DOI: https://doi.org/10.1039/d4ce00435c
IF: 3.756
2024-05-26
CrystEngComm
Abstract:In this study, three supramolecular compounds, namely [Na(18-crown-6)]ReO4 (1), [K(18-crown-6)]ReO4 (2) and [NH4(15-crown-5)2]ReO4 (3) were synthesized and characterized using microanalysis, thermogravimetric, differential scanning calorimetry and powder X-ray diffraction techniques, among others. Herein, 15-crown-5 and 18-crown-6 represent 1,4,7,10,13-pentaoxacyclopentadecane and 1,4,7,10,13,16-hexaoxacyclooctadecane, respectively. Both 1 and 2 experienced one-step reversible phase transition at ~436 K and ~360 K, respectively, while 3 underwent three steps of reversible phase transitions at ~289 K, ~352 K and ~380 K. A dielectric anomaly occurred at ~433 K (~363 K) for 1 (2), consistent with the temperature obtained from DSC measurement. In the dielectric spectra of 3, anomalies were observed at ~386 K and ~433 K, corresponding to two thermal anomalies observed at higher temperatures in the DSC plot. However, there was an absence of dielectric response around 289 K where a thermal anomaly appeared in the DSC plot. The distinct crystal structures, phase transition and dielectric properties in 13 stem from the degree of compatibility between the radii of M+ (Na+, K+ and NH4+) and the ring sizes of crown ethers (18-crown-6 and 15-crown-5).
chemistry, multidisciplinary,crystallography