Investigating the effect of graphene oxide on the physical and mechanical properties of high-strength rubberized concrete using RStudio

Gyanendra Kumar Chaturvedy,Umesh Kumar Pandey

DOI: https://doi.org/10.1007/s41939-023-00209-1

2023-08-14

Abstract:The scarcity of natural aggregate (NA) is a great challenge for the fast-growing construction industries. Rubber aggregate (RA), obtained from the vehicles’ tire rubber, can be a better alternative. Rubberized concrete (RC), made after the inclusion of RA in concrete, is considered a greener and more sustainable substitute for conventional concrete. The physical and mechanical properties of RC, viz. workability, density, air content, compressive strength, tensile strength, and flexural strength, have been analyzed experimentally, and numerical simulation was performed on these experimental results with the help of RStudio software. A concrete mix design having a water-cement ratio of 0.25 was prepared with a target mean strength of 70 MPa in which RA varied as 0–15% of manufactured sand (MS) and GO varied as 0–0.1% of cement by weight proportions. RA content linearly decreases the concrete's workability, density, compressive strength, tensile strength, and flexural strength; while increasing the air content. Incorporating GO in the RC increases the density, compressive strength, tensile strength, and flexural strength of the RC after mitigating the RA’s effect in the concrete. Workability and air content tend to decrease with the action of GO in the RC. For the development of high-strength RC, RA and GO contents are suggested to fix at 10% of MS and 0.05% of cement by weight, respectively. The numerical simulations by RStudio state that the physical and mechanical properties of the GO-induced RC rely on the independent variables (RA and GO) and are highly correlated, according to the predicted model developed using R Studio.