Abstract:Eugenol, an abundant, naturally occurring phenolic compound, was converted into a thermoplastic polycarbonate by olefin metathesis followed by interfacial polymerization with triphosghene. This resulted in polymers with Mn ranging from 5300 – 12700 g mol-1 and an average glass transition temperature (Tg) of 82 °C. The polycarbonates were depolymerized via ethenolysis reactions under modest ethylene pressures (150 – 240 psi) in the presence of [Ru]-metathesis catalysts to yield a discrete monomer [bis(4-allyl-2-methoxyphenol) carbonate, compound 2]. 2 was then polymerized with a second generation Grubbs catalyst (M204) to produce a recycled polymer with Mn = 7500 g mol-1 and a Tg of 114 °C. The 32 °C increase in Tg was due to the isomerization of the allyl group to internal positions, which then allowed for the formation of stilbene and 3-carbon unsaturated linkages between aromatic groups. To expand the ethenolysis recycling approach to cross-linked networks, eugenol was converted into a cyanate ester (3), which was then thermally cyclotrimerized to generate 2,4,6-tris(4-allyl-2-methoxyphenoxy)-1,3,5-triazine (4), a monomer with a triazine core and three pendent aromatic rings with methoxy and allyl substituents. 4 was cross-linked via olefin metathesis (M204 catalyst) to generate a network with Mn = 8600 g mol-1 and a Tg of 180 °C. Similar to the polycarbonate, the polycyanurate was efficiently depolymerized in the presence of ethylene to regenerate 4. Compound 4 was then polymerized and depolymerized two additional times, demonstrating full circularity for the triazine monomer/network. The recycled networks exhibited similar Tgs (167–184 °C) and thermal stability compared to the virgin polymer. Overall, this work demonstrates that both thermoplastic and cross-linked networks can be readily prepared from eugenol and catalytically recycled under standard ethenolysis conditions. Unlike many conventional approaches, the recycled polymers described in this work exhibited no significant degradation in thermomechanical properties. This type of approach supports a circular bioeconomy and may help to reduce plastic waste and the accumulation of micro/nanoplastic particles in the environment.

Functionalizable and Recyclable Aliphatic Polycarbonates Derived from Biomass Feedstocks and CO2

Biobased Bifunctional Monomers toward Functionalizable Polycarbonates and Poly(cyclic olefin)s with Tunable Properties

Pinwheel-Shaped Tetranuclear Organoboron Catalysts for Perfectly Alternating Copolymerization of CO2 and Epichlorohydrin.

A Bifunctional Β-Diiminate Zinc Catalyst with CO2/Epoxides Copolymerization and RAFT Polymerization Capacities for Versatile Block Copolymers Construction

Highly Selective Preparation and Depolymerization of Chemically Recyclable Poly(cyclopentene Carbonate) Enabled by Organoboron Catalysts.

Highly Efficient Enzymatic Catalysis for Cyclocarbonate Polymerization

Multifunctional Linear And Hyperbranched Five-Membered Cyclic Carbonate-Based Polymers Directly Generated From Co2 And Alkyne-Based Three-Component Polymerization

CO2 and Lignin‐Based Sustainable Polymers with Closed‐Loop Chemical Recycling

Chemical Synthesis of CO 2 -Based Polymers with Enhanced Thermal Stability and Unexpected Recyclability from Biosourced Monomers

High Molar Mass Polycarbonates as Closed-Loop Recyclable Thermoplastics

Functional and Degradable Polyester- co -polyethers from CO 2 , Butadiene, and Epoxides

Aliphatic Polyketones Via Cross-Metathesis Polymerization: Synthesis and Post-Polymerization Modification

Biorenewable and circular polyolefin thermoplastic elastomers

[Ru]-Catalyzed Olefin Metathesis and Ethenolysis for the Synthesis and Recycling of Bio-Based Polycarbonates and Polycyanurates

CO2-Based Polycarbonates through Ring-Opening Polymerization of Cyclic Carbonates Promoted by a NHC-Based Zinc Complex

Aliphatic Polycarbonates from Cyclic Carbonate Monomers and Their Application as Biomaterials

High-Performance Chemically Recyclable Multifunctional Polyolefin-Like Biomass-Derived Polyester Materials

Chemical Recycling of Poly(cyclohexene carbonate)s via Synergistic Catalysis

Crystalline Stereoregular Poly(ether-ester) via MeAl[Salen]-Catalyzed Well-Controlled Ring-Opening Polymerization of Enantiopure Cyclic Ether-Ester Monomer

A versatile strategy to main chain sulfur/selenium functionalized polycarbonates via macro-ring closure of diols and subsequent ring-opening polymerization.