Mechanochemical Synthesis of MOF-303 and Its CO2 Adsorption at Ambient Conditions

Sylwia Głowniak,Barbara Szczęśniak,Jerzy Choma,Mietek Jaroniec

DOI: https://doi.org/10.3390/molecules29112698

IF: 4.6

2024-06-07

Molecules

Abstract:Metal–organic structures have great potential for practical applications in many areas. However, their widespread use is often hindered by time-consuming and expensive synthesis procedures that often involve hazardous solvents and, therefore, generate wastes that need to be remediated and/or recycled. The development of cleaner, safer, and more sustainable synthesis methods is extremely important and is needed in the context of green chemistry. In this work, a facile mechanochemical method involving water-assisted ball milling was used for the synthesis of MOF-303. The obtained MOF-303 exhibited a high specific surface area of 1180 m2/g and showed an excellent CO2 adsorption capacity of 9.5 mmol/g at 0 °C and under 1 bar.

chemistry, multidisciplinary,biochemistry & molecular biology

What problem does this paper attempt to address?

The main purpose of this paper is to study the application of mechanochemical synthesis methods in the preparation of metal-organic framework materials (MOFs) and to explore their carbon dioxide adsorption performance under environmentally friendly conditions. Specifically, the paper demonstrates the advantages of mechanochemical synthesis methods by comparing the physicochemical properties of three materials, MOF-303, ZIF-8, and CuBTC, prepared by different synthesis methods (solvent method and mechanochemical method).

The core issues of the paper are:
1. **Developing environmentally friendly synthesis methods**: Traditional MOF synthesis methods usually require the use of harmful solvents and generate a large amount of waste. Therefore, researchers are committed to developing more environmentally friendly and efficient synthesis methods.
2. **Improving the performance of MOF materials**: MOF-303 synthesized by the mechanochemical method exhibits excellent carbon dioxide adsorption capacity, reaching 9.5 mmol/g at room temperature and pressure, which is higher than that of MOF materials synthesized by traditional methods.

The paper also discusses in detail the effects of mechanochemical synthesis conditions (such as ball milling time, speed, and purification time) on the structure and performance of MOF-303. The experimental results show that the optimal mechanochemical synthesis conditions are: 1 hour of ball milling time, 500 rpm rotation speed, and 48 hours of methanol purification time. MOF-303 synthesized under these conditions has a higher specific surface area (1180 m²/g) and better pore structure. In addition, the paper compares the differences in morphology, crystallinity, and pore structure of MOF materials obtained by different synthesis methods.