Abstract:In order to realize the utilization of coal-fired solid waste and captured carbon dioxide, the effects of ratio of solid waste, mineralized curing pressure and mineralized curing temperature on the compressive strength and carbon fixation rate of aerated concrete were studied, with the coal-based waste, coal ash and desulfurization gypsum as the main raw materials and slag as the supplementary cementitious material. The crystal phase structure and micro morphology under different mineralized curing conditions were analyzed by XRD and SEM, and the effect of different mineralized curing conditions on the pore structure of aerated concrete was studied by MIP. The experimental results show that the appropriate residual water/slag ratio is helpful to improve the CO 2 fixation rate and early compressive strength of aerated concrete. When the CO 2 curing pressure increases from 0.05 MPa to 1.00 MPa, the carbon fixation rate increases by 24.8%, and the compressive strength increases first and then decreases. When the curing pressure is 0.1 MPa, the maximum compressive strength is reached. With the CO 2 curing temperature rising from 25 ℃ to 105 ℃, the carbon fixation rate and compressive strength increases first and then decreases. The carbon fixation rate reaches maximum of 7.21% at 45 ℃, and the compressive strength reaches maximum of 3.53 MPa at 65 ℃. According to analysis of XRD and SEM, the major mineralized products are CaCO 3 , which mainly exist in the form of calcite and vaterite. Higher curing pressure（≥0.2 MPa） is likely to cause micro-cracks at the product interface. With the increase of curing temperature, the mineralized products and hydrated products appear simultaneously. According to MIP analysis, the influence of mineralized curing on the pores of aerated concrete can be divided into two aspects: on the one hand, CaCO 3 and other products with small particle size can fill the pores of 10-50 nm, on the other hand, reaction heat of mineralization and volumetric expansion of products can cause the increase of 30-60 μm pores. The microstructure can be optimized by increasing the curing temperature, which can make the distribution of pores more uniform.

An industrial demonstration study on CO2 mineralization curing for concrete

Carbonation Curing of Industrial Solid Waste‐based Aerated Concretes

Sustainable Building Material from CO2 Mineralization Slag: Aggregate for Concretes and Effect of CO2 Curing

Enhanced Carbonation Curing of Cement Pastes with Dolomite Additive

An Overview on the Influence of Various Parameters on the Fabrication and Engineering Properties of CO2-cured Cement-Based Composites

Microstructure Refinement of Calcium-Sulfate-aluminate and Portland Cement (CSA-PC) Hybrids with Accelerated CO2 Curing (ACC)

Accelerated Mineral Carbonation Curing of Cement Paste for CO2 Sequestration and Enhanced Properties of Blended Calcium Silicate

Effects of Curing Regimes on Calcium Oxide–Belite–Calcium Sulfoaluminate-Based Aerated Concrete

Carbonation curing of mortars produced with reactivated cementitious materials for CO2 sequestration

Enlightenment of Ancient Tabia for Sustainable Construction Material Manufacture by Accelerated CO2 Treatment

Study on formulation of aerated concrete by CO2 mineralization using coal ash

Effect of Mixing and Curing System on Carbon Fixation Amount and Performance of Circulating Fluidized Bed Fly Ash Cement Cementitious Material System

Review on CO2 curing of non-hydraulic calcium silicates cements: Mechanism, carbonation and performance

Carbonation curing for wollastonite-Portland cementitious materials: CO2 sequestration potential and feasibility assessment

CO2 Pretreatment to Aerated Concrete with High-Volume Industry Wastes Enables a Sustainable Precast Concrete Industry

An overview of utilizing CO2 for accelerated carbonation treatment in the concrete industry

Life-cycle Assessment of Emerging CO2 Mineral Carbonation-Cured Concrete Blocks: Comparative Analysis of CO2 Reduction Potential and Optimization of Environmental Impacts

Effect of Carbonation Treatment on the Strength and CO2 Uptake Rate of Composite Cementitious Material with a High Steel Slag Powder Content

Superior CO<sub>2</sub> uptake and enhanced compressive strength for carbonation curing of cement-based materials via flue gas

Steel Slag Accelerated Carbonation Curing for High-Carbonation Precast Concrete Development

Research status of building materials utilization and CO2 curing technology on typical coal-based solid waste: A critical review