Bioinspired fiberboard-and-mortar structural nanocomposite based on ultralong hydroxyapatite nanowires with high mechanical performance

Han-Ping Yu,Ying-Jie Zhu,Zhi-Chao Xiong,Bing-Qiang Lu
DOI: https://doi.org/10.1016/j.cej.2020.125666
IF: 15.1
2020-11-01
Chemical Engineering Journal
Abstract:<p>Natural materials have enlightened us to assemble brittle building blocks into specific architectures with both high strength and toughness. As the main inorganic component of the bone and tooth, hydroxyapatite (HAP) materials have a high biocompatibility, but usually have a high brittleness. It is still a big challenge to artificially prepare biomaterials with the combination of high strength and high toughness, similar to natural materials constructed with brittle HAP building blocks. In this work, considering that enamel and nacre are typical examples of natural biomaterials with high strength and high toughness, respectively, we combine the structural merits of both enamel (highly ordered bundles) and nacre (brick-and-mortar structure) to construct a new kind of highly ordered ultralong HAP nanowire fiberboard-and-mortar alignment hierarchical structure (HFMAS) by the multiscale and multilevel assemblies of ultralong HAP nanowires from the nanoscale to microscale to macroscale and from one-dimensional (1-D) to 2-D to 3-D levels. The as-prepared hierarchical HFMAS nanocomposite can achieve a confluence of strengthening and toughening mechanisms of enamel and nacre, and exhibits superior mechanical properties such as high strength (308 MPa), Young's modulus (34.7 GPa), and toughness (4.77 MPa·m<sup>1/2</sup>), which are far better than those of many synthetic HAP-organic composites and other materials reported in the literature. Moreover, the as-prepared HFMAS nanocomposite exhibits a low density (1.8 g cm<sup>−3</sup>), good resistance to great impact, good damping capacity and durability. The as-prepared HFMAS nanocomposite is promising for various applications such as the protective armor, mechanical damping, and building materials.</p>
engineering, chemical, environmental
What problem does this paper attempt to address?
The problem this paper attempts to address is how to artificially create bio-materials with high strength and toughness. Specifically, the goal of the paper is to construct a highly ordered fiberboard-mortar structured nanocomposite material (HFMAS) based on ultra-long hydroxyapatite nanowires by mimicking the structural characteristics of natural materials (such as enamel and nacre) to achieve high mechanical performance, including high strength, high modulus, and high toughness. ### Background of the Paper - **Inspiration from Natural Materials**: Materials in nature, such as bones, teeth, and nacre, can assemble brittle components into specific structures, thereby exhibiting high strength and high toughness. - **Characteristics of Hydroxyapatite (HAP)**: HAP is the main inorganic component of bones and teeth, with high biocompatibility but usually very brittle. Therefore, artificially synthesizing HAP-based materials with high strength and toughness is a significant challenge. ### Research Objectives - **Combining the Advantages of Enamel and Nacre**: Enamel has a highly ordered nanorod bundle structure, while nacre has a brick-mortar structure. The paper combines the advantages of these two structures through a multi-scale and multi-level self-assembly process to construct a new HFMAS nanocomposite material. - **Improving Mechanical Performance**: Through this structural design, the HFMAS nanocomposite material exhibits excellent performance in terms of strength, modulus, and toughness, far superior to many reported synthetic HAP-organic composites and other materials. ### Experimental Methods - **Synthesis of Ultra-long HAP Nanowires**: Ultra-long HAP nanowires were synthesized through a solvothermal method using calcium oleate precursors. - **Preparation of Macroscopic Fibers**: Highly ordered ultra-long HAP nanowires were assembled into macroscopic fibers using a simple injection method. - **Preparation of Nanocomposite Materials**: Fiberboards were formed by compressing the parallel-aligned macroscopic fibers, and the polymer phase (PMMA and PAA) was filled into the HAP nanowire framework, ultimately forming the HFMAS nanocomposite material. ### Main Results - **Mechanical Performance**: The strength of the HFMAS nanocomposite material reached 308 MPa, the Young's modulus was 34.7 GPa, and the toughness was 4.77 MPa·m^1/2. These properties are far superior to many reported synthetic HAP-organic composites. - **Other Properties**: The HFMAS nanocomposite material also exhibited low density (1.8 g/cm³), good impact resistance, good damping capacity, and durability. ### Application Prospects - **Protective Armor**: Due to its high strength and toughness and low density, the HFMAS nanocomposite material is promising for use in protective armor. - **Mechanical Damping**: Its good damping capacity makes it suitable for mechanical damping applications. - **Building Materials**: Its excellent mechanical performance and durability also make it potentially applicable in the field of building materials. In summary, by mimicking the structural characteristics of natural materials, this paper successfully prepared a HAP-based nanocomposite material with high strength and toughness, providing new ideas for the design and preparation of high-performance bio-materials.