A Solvent-Free Process Enabled by Polytetrafluoroethlyene/Carbon Black Composites for Fabricating Electrodes for Lithium-Ion Batteries with a High Volumetric Energy

Hyeongjun Choi,Dongjun Moon,Junmyoung Sheem,Jin Kyo Koo,Seungmin Hong,Seung-Min Oh,Young-Jun Kim,Seoungmin Hong,Seoung-Min Oh
DOI: https://doi.org/10.1149/1945-7111/acf525
IF: 3.9
2023-08-31
Journal of The Electrochemical Society
Abstract:Manufacturing electrodes for lithium-ion batteries (LIBs) consists of making a slurry, coating the slurry onto a current collector, drying the slurry to remove solvent, and calendaring the electrode. Cathodes for LIBs are fabricated by a wet process using a toxic chemical, N-methyl-2-pyrrolidone (NMP). It is preferable to use a dry process without toxic chemicals, and with fewer manufacturing operations, which saves money, but the powder-mixing step of the dry process makes it difficult to ensure a uniform distribution of the carbonaceous conducting agents and binder used, which agglomerate in the dry mixed product. To solve this problem, we fabricate a composite of polytetrafluoroethylene (PTFE) and carbon black (CB) nanoparticles. The electrode fabricated using the PTFE/CB composite has a 98 wt% active material content and 3.8 g cc‒1 of electrode density. An electrode produced by the conventional wet process using a polyvinylidene fluoride binder and NMP solvent has a 96 wt% active material content and an electrode density of 3.4 g cc‒1. The dry-processed electrode has a higher volumetric capacity (760 mAh cc−1) as well as a higher discharge rate capability and cycle life than a conventional wet-processed electrode.
electrochemistry,materials science, coatings & films
What problem does this paper attempt to address?