Abstract:An efficient reduction method to obtain high-quality graphene sheets from mass-producible graphene oxide is highly desirable for practical applications. Here, we report an in situ deoxidation and graphitization mechanism for graphene oxide that allows for high-quality reduced graphene oxide sheets under the low temperature condition (<300 °C) by utilizing a well-known Fischer–Tropsch reaction catalyst (CuFeO2). By applying modified FTR conditions, where graphene oxide was reduced on the catalyst surface under the hydrogen-poor condition, deoxidation with much suppressed carbon loss was possible, resulting in high-quality graphene sheets. Our experimental data and density functional theory calculations proved that reduction which occurred on the CuFeO2 surface preferentially removed adsorbed oxygen atoms in graphene oxide sheets, leaving dissociated carbon structures to be restored to a near-perfect few-layer graphene sheet. TGA-mass data revealed that GO with catalysts released 92.8% less carbon-containing gases than GO without catalysts during the reduction process, which suggests that this process suppressed carbon loss in graphene oxide sheets, leading to near-perfect graphene. The amount of oxygen related to the epoxide group in the basal plane of GO significantly decreased to near zero (from 43.84 to 0.48 at. %) in catalyst-assisted reduced graphene oxide (CA-rGO). The average domain size and the density of defects of CA-rGO were 4 times larger and 0.1 times lower than those for thermally reduced graphene oxide (TrGO), respectively. As a result, CA-rGO had a 246 and 8 times lower electrical resistance than TrGO and CVD-graphene. With these performances, CA-rGO coated paper connected to a coin-cell battery successfully lit an LED bulb, and CA-rGO itself acted as an efficient catalyst for both the hydrogen evolution reaction and the oxygen evolution reaction.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c02178?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c02178</a>.SEM, TEM, and AFM images of catalysts and GO; additional data of CA-rGO (Raman, optical image, XRD, and electrical data); ID/IG ratio, XPS, UV–vis spectra, FT-IR spectra of samples prepared with different conditions; GC-mass analysis, TOF-SIMS, and ICP data for the reduction mechanism (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02178/suppl_file/nn1c02178_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Production of reduced graphene oxide from activated rice husk charcoal using a high-energy ball milling method

Fabrication and Optimization of Activated Carbons-Based Graphene Oxide from Rice Husks as an Alternative to Graphite

Synthesis of graphene oxide from graphite by ball milling

Sustainable Synthesis of High-Surface-Area Graphite Oxide via Dry Ball Milling

Efficient preparation and characterization of graphene based on ball milling

Oil Palm Waste-Based Precursors as a Renewable and Economical Carbon Sources for the Preparation of Reduced Graphene Oxide from Graphene Oxide

Rapid Effective Reduction by Microwave-Irradiated Thermal Reaction for Large-Scale Production of High-Quality Reduced Graphene Oxide

Large scale synthesis of 2D graphene oxide by mechanical milling of 3D carbon nanoparticles in air

Rice husk char as a sustainable material for the preparation of graphene oxide-supported biocarbons with mesoporous structure: A characterization and adsorption study

Preparation of reduced Graphene Oxide (rGO) assisted by microwave irradiation and hydrothermal for reduction methods

Simple and low‐cost preparation of functionalised graphene by microwave expansion combined with ball milling grafting

Scalable production of high-quality exfoliated graphene using mechanical milling in conjugation with supercritical CO2

Preparation of Reduced Graphene Oxide by Infrared Irradiation Induced Photothermal Reduction

Graphitization with Suppressed Carbon Loss for High-Quality Reduced Graphene Oxide

A sustainable route for production of graphene oxide-contained nanostructured carbons from rice husk waste and its application in wastewater treatment

Production of activated and Graphene-Like Carbon Materials from rice husk

Sustainable and Cost-Efficient Production of Micro-Patterned Reduced Graphene Oxide on Graphene Oxide Films

A Facile and Cost-Effective Approach to the Reduction of Exfoliated Graphite Oxide Using Sodium Hypophosphite under Acidic Conditions

Highly Efficient Preparation of Graphite Oxide without Water Enhanced Oxidation

High-strength reduced graphene oxide paper prepared by a simple and efficient method

Large-scale Production of Few-Layer Reduced Graphene Oxide by the Rapid Thermal Reduction of Graphene Oxide and Its Structural Characterization