Preparation of porous iridium-ruthenium-based acidic water oxidation catalyst by ascorbic acid reduction and evaporation

Hui Chen,Runxu Deng,Shixin Gao,Feng Liu

DOI: https://doi.org/10.1088/1742-6596/2566/1/012017

2023-08-20

Journal of Physics: Conference Series

Abstract:Green hydrogen is the ultimate direction for energy development technology. Hereon, the porous materials of promoted iridium-ruthenium-based catalyst were prepared by ascorbic acid reduction and evaporation drying methods. The unsupported iridium ruthenium-based catalysts were porous structures, characterized by scanning electron microscopes (SEM). In 0.5 mol·L −1 H 2 SO 4 , the electrochemical oxygen precipitation reaction overpotential was only 251 mV at 10 mA·cm 2 , compared to commercial 303 mV. The polarization overpotential was not significantly reduced, after 20 000 cycles of accelerated cyclic aging experiments. The porous structure of the iridium-ruthenium-based catalysts showed higher catalytic activity for oxygen precipitation than the commercial IrO 2 (ZrO 2 ) catalysts. Porous materials could improve the activity of catalysts, which provides a good research idea for the synthesis of electrocatalysts.