Enhanced Separation Performance of Radioactive Cesium and Cobalt in Graphene Oxide Membrane via Cationic Control

Zuyan Hu,Shuai Wang,Yizhou Yang,Feng Zhou,Shanshan Liang,Liang Chen

DOI: https://doi.org/10.1021/acs.langmuir.1c02656

IF: 3.9

2022-02-03

Langmuir

Abstract:The great applications of nuclear power for the most promising clean energy sources have been challenged by a large amount of radioactive wastewater generated, specifically the Cs+/Co2+ separation for nuclear waste storage, retreatment or recycling of radioactive wastewater, because of their wide difference in half-life and high heat release. In this work, graphene oxide membranes (GOMs) with interlayer spacing controlled by cations were used to separate mixed Cs+/Co2+ ions. The separation factors of Cs+/Co2+ for K+-controlled graphene oxide membranes (K-GOMs) was 2∼3 times higher than that of GOMs without treatment. In addition, the separation factors of Cs+/Co2+ for K-GOMs can be further enhanced with the increase of membranes thickness and change the initial ratios of the two ions. Typically, the separation factors of K-GOMs with a thickness of ∼300 nm reached up to 73.7 ± 3.9. Moreover, the K-GOM showed outstanding stability of the separation performance under long-term operation within 7 days. First-principles calculation revealed that the enhanced ionic selectivity of controlled GOM is induced by the difference of adsorption energies between the hydrated cations and aromatic rings, resulting in a significant increase in the mobility differences between Cs+ and Co2+ through a fixed narrow interlayer spacing. This study demonstrated excellent separation performances of GO-based membranes based on their size-exclusion effect rather than electrostatic repulsion effect, and we believe this work can enable potential efficient treatment technologies for radioactive wastewater needed urgently.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.langmuir.1c02656.Schematics of the experimental setups for single-ion permeation test (Figure S1); schematics of the experimental setups for Cs+/Co2+ separation test (Figure S2); the photos of water flux experiment (Figure S3); calculation of ions adsorption on different sites of a finite-size graphite surface (Figure S4); the zeta potential of GO solution, and GO with KCl solution (Figure S5); X-ray diffraction of GOM immersed in KCl solution with different time (Figure S6); the permeation rates of different single ion for GOM and K-GOM (Figure S7); detailed information for performance comparison of monovalent ion permeation rates versus separation factors of monovalent/divalent ion for GO-based membranes reported in literature. (Table S1); water fluxes of GOM and K-GOM for separation Cs+/Co2+ (Figure S8); the ions permeability and the separation factor (SF) of Cs+ and Co2+ using K-GOM with different membrane thickness. (Table S2); the effect of membrane thickness on separation factors of Cs+/Co2+ for GOM and K-GOM (Figure S9); the ions permeability and the separation factor (SF) of Cs+ and Co2+ using K-GOM with different membrane thickness. (Table S3); the mechanical strength of the GOM immersed in KCl solutions and DI water for 10 days (Figure S10); the most stable optimized geometries of K+–(H2O)6, Cs+–(H2O)6 and Co2+–(H2O)6 (Figure S11); ultraviolet spectra of GO solution mixed with Cs+/Co2+/K+ (Figure S12); X-ray diffraction for GO membranes immersed in pure water and in various solutions (Figure S13) (PDF)This article has not yet been cited by other publications.

chemistry, multidisciplinary, physical,materials science