Enhanced photoelectrochemical activity of bi-functional photocatalytic fuel cell by a superior heterostructure SnO 2 /BiOBr/MoS 2 photoanode

Yun He,Longkai Zhu,Jue Hu,Yizhen Zhang,Jiaqi Wang,Chengxu Zhang,Jianfen Li,Michael K.H. Leung,Hui Li

DOI: https://doi.org/10.1016/j.apsusc.2023.156821

IF: 6.7

2023-03-16

Applied Surface Science

Abstract:A dual-photoelectrode PFC system was constructed using an excellent SnO 2 /BiOBr/MoS 2 as a photoanode and copper oxide/copper as a photocathode for the first time. The appropriate interfacial contact and outstanding photoelectrochemical activity of the photoanode can be attributed to SnO 2 hole-blocking layer. It is not only employed as a conductive scaffold for BiOBr/MoS 2 but also provided less tendency for charge transport loss. In addition, the by-product Bi 2 S 3 acts as a sensitizer due to its broad absorption spectrum (∼800 nm) to increase light harvesting. The resulting SnO 2 /BiOBr/MoS 2 photoanode yields the highest photocurrent density at all bias voltages and achieves 4.0 mA cm −2 , which is around eight times higher in comparison with bare BiOBr while it is twice as much as that of the BiOBr/MoS 2 photoanode without SnO 2 hole reflection layer. This study demonstrates that recombination is significantly inhibited by adding methylene blue (MB) as the hole scavenger, resulting in a high power output efficiency in the dual-photoelectrode PFC system. An ultrahigh power density of 0.045 mW cm −2 and improved photodegradation efficiency to reach ∼ 91 % after 180 min. The excellent power density can therefore be assumed that the enriched strong oxidizing photoexcited holes were used to participate in directly decomposing MB.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films