Abstract:The booming electrolytic manganese industry has brought a huge amount of electrolytic manganese anode mud (EMAM). The management and value-added recovery of EMAM were very important for environmental improvement and economic benefits. In this study, EMAM is used as a cost-effective raw material. Firstly, the manganese-containing solution was obtained by reducing acid leaching with EMAM. Then, Li1.2Ni0.2Mn0.6O2 (Z-LNMO) cathode materials were prepared from a manganese-containing solution by co-precipitation process. Finally, to enhance the performance of the Z-LNMO materials, surfactants (C12H25SO4Na, C10H14N2Na2O8, C18H29NaO3S, C19H42BrN) were introduced in the preparation of precursor materials to obtain the material with higher crystallinity. ICP results showed that S/Fe ions of EMAM were retained in Z-LNMO materials. Moreover, the Z-LNMO sample shows a stoichiometric similar element content to Li1.2Ni0.18Fe0.02Mn0.6O1.96S0.04. EDS results show that S/Fe ions were uniformly distributed in Z-LNMO materials. The shift of XRD peak further indicates that the use of EMAM waste is expected to directly obtain S/Fe ions doped lithium-rich manganese-based cathode materials. The first-principle calculation shows that the S/Fe ions as the doping source make the transfer of excited electrons from the valence band to the conduction band easier, thereby enhancing the conductivity of the materials. The CV curve and differential capacity (dQ/dV) curve show that the Z-LNMO material prepared by EMAM inhibits the excessive oxidation of Li2MnO3 to a certain extent, thus providing excellent reversible capacity and stabilizing the material structure. Electrochemical evaluation reveals that the Z-LNMO materials prepared with the EMAM exhibit superior cycling stability (112% after 100 cycles at 0.1C). Moreover, the introduction of C10H14N2Na2O8 (EDTA-2Na) and C12H25SO4Na (SDS) in the preparation of precursor materials can improve the first discharge-specific capacity and stability of materials by modifying the morphology of precursor materials (refine particles). Among them, the materials modified by EDTA-2Na show the best performance, and the particle size is about 200 nm. Compared with the original materials, the improved first discharge-specific capacity (218.6 mAh g−1 at 0.1C) and capacity retention (245.8 mAh g−1 after 100 cycles) of the materials modified with EDTA-2Na were improved. The EIS results also confirm that the introduction of EDTA-2Na effectively decreases the charge transfer resistance and facilitates the Li diffusion of the as-prepared cathode materials. This work confirmed the possibility of extracting manganese from EMAM to prepare lithium-rich manganese-based cathode materials, and provided a new promising way for the efficient value-added utilization of EMAM.

Enhanced removal of Pb from electrolytic manganese anode slime and preparation of chemical MnO 2

Enhanced Leaching of Mn from Electrolytic Manganese Anode Slime via an Electric Field

Volatilization of Zn and Pb and Preparation of Integrated Micro-Electrolysis Filter from Copper Slag and Its Application for Removing Cr(VI) from Aqueous Solution.

Effective Removal of Sb(V) from Aqueous Solutions by Electrocoagulation with Composite Scrap Iron-Manganese As an Anode.

Enhanced manganese leaching from electrolytic manganese residue by electrochemical process and Na2SO3

Enhanced removal of Mn2+ and NH4+-N in electrolytic manganese metal residue using washing and electrolytic oxidation

Efficient recovery and utilization of electrolytic manganese anode mud- preparation of high-performance Li1.2Ni0.2Mn0.6O2 cathode material for lithium-ion batteries

Enhanced removal of Mn2+ and NH4+-N in electrolytic manganese residue leachate by electrochemical and modified phosphate ore flotation tailings

Highly efficient Mn2+, Mg2+, and NH4+ recovery from electrolytic manganese residue via leaching, solvent extraction, coprecipitation, and atmospheric oxidation

A Novel Circulation Process to Effectively Produce Electrolytic Manganese Metal (EMM) with Low-Grade Manganese Oxide Ores and High-Sulfur Manganese Ores

Insight into mechanisms of Mn and NH 4 + -N removal with recovery of Mn and Mg from electrolysis manganese residue (EMR): Effect of humus and NaOH

Fe Doped Γ-Mno2 of Anode for Lead Release Inhibition in Zinc Electrowinning

Study on harmless treatment of electrolytic manganese residue by low temperature thermochemical method

Recovery of manganese as spinel MgMn2O4 cathode material from electrolytic manganese residue by Na2CO3 hydrothermal-roasting process

Recovery and Utilization of Lead in Lead–Containing Waste Residue from Electrolytic Manganese Production

Electrodeposition of Manganese Metal and Co-production of Electrolytic Manganese Dioxide Using Single-membrane Double-chamber Electrolysis

Desulfurization of Rejected Electrolytic Manganese Metal by Electroslag Remelting Furnace with a Water-Cooled Electrode

Ammonia removal and simultaneous immobilization of manganese and magnesium from electrolytic manganese residue by a low-temperature CaO roasting process

Efficient and clean manganese electrowinning in an anion-exchange membrane electrolyzer by pulse current electrodeposition method

A Novel Functional Lead-Based Anode for Efficient Lead Dissolution Inhibition and Slime Generation Reduction in Zinc Electrowinning

Self-formed MnCO3/FeS2@SiO2 in modified electrolytic manganese residues as an enhanced peroxymonosulfate activator for ammonium dibutyl dithiophosphate removal