Abstract:This study investigates the impact of thermomechanical processing route on the microstructural evolution, and mechanical properties (tensile strength, hardness and elastic plastic (J 1c ) fracture toughness) of the 7075-aluminum alloy. As received 7075 Al Alloy underwent for the solution heat treatment (SHT) followed by artificial aging and cold rolling (CR) process, respectively. Generally, it was observed that cold rolling of 7075 Al alloy is very challenging, but in this work 90 % cold rolling successfully achieved by optimizing the thermo-mechanical process. The novel heat treatment process for achieving the 90 % cold rolling reduction as follow: firstly, SHT was performed at 470°C for 8 hours(h), there after aging at 140°C for 21 h was performed. Characterization techniques like X-ray diffraction (XRD), optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) was employed to assess the microstructure and phase constituents. Elastic plastic (J 1c ) fracture toughness was studied well on SHT, peak aged and rolled sample. Additionally, Vickers hardness and tensile test were performed. Aging and Cold rolling treatment effectively enhanced tensile strength and hardness ascribed to formation of fine rod shape precipitates of η"(Mg 2 Zn 3 ) and formation of sub grains with localized strain accumulation, respectively Split diffraction spots with satellite pattern in long range ordering has also observed in selected area electron diffraction (SAED) pattern of η" attributable to stacking faults and periodic arrangement of precipitates, respectively, as a consequence of this 90 % cold rolling of 7075 Al alloy was accomplished. The maximum Vickers hardness, Tensile strength and Elastic plastic (J 1c ) fracture toughness values were achieved after SHT (470°C for 2 h), peak aged (PA) (140°C for 21 h) and 90 % cold rolling are 226 HV, 526 MPa and 344.54 kJ/m 2 , respectively.

Evolution of microstructure and properties of AA 7072/7075/7072 composite sheets during various finish rolling temperature

Microstructure and Properties Evolution of 7075 Al alloy in Hot Rolling and Short Process Heat Treatment

Effects Of Rolling Process On Microstructure And Mechanical Property Of 7050 Aluminum Alloy

High-Temperature Tensile Mechanical Properties and Microstructure of Rolled 6082-T6 Aluminum Alloy Sheets

Effects of Rolling Temperature on Hot Rolling Behaviors and Mechanical Properties of ABOw/6061Al Composites

Edge-crack free and high mechanical properties of AA7075 sheets by using cryorolling and subsequent aging

Mechanical Property and Microstructure of Rolled 7075 Alloy under Hot Compression with Different Original Grains

Effects of cryorolling, room temperature rolling and aging treatment on mechanical and corrosion properties of 7050 aluminum alloy

Effects of microstructure on tensile properties of AA2050-T84 Al-Li alloy

Effect of thermomechanical processing on mechanical properties and microstructural evolution of Al-Mg-Zn alloy

Microstructure Evolution of the Near-Surface Deformed Layer and Corrosion Behavior of Hot Rolled AA7050 Aluminum Alloy

Microstructural Evolution and Mechanical Properties of Pure Aluminum upon Multi-Pass Caliber Rolling

Evolution of Microstructures and Textures of 7050 Al Alloy Hot-Rolled Plate During Staged Solution Heat-Treatments

Effects of the Rolling Temperature on Microstructure and Mechanical Properties of 2cr13/316l Laminated Composites Prepared by Accumulative Roll-Bonding (ARB)

Microstructure Evolution and Enhanced Mechanical Properties of As-Rolled TiB/(TA15-Si) Composite Via Heat Treatment

Effect of Finishing Temperature on Microstructure of 7050 Aluminum Alloy During Hot-Compression Deformation

Influence of different rolling processes on the microstructures and mechanical properties of 6016 aluminum alloy

Hot tensile deformation behavior and microstructure evolution of 7075 aluminum alloy sheet

Microstructure and mechanical properties of AA1050/AA6061 multilayer composites via accumulative roll bonding and cryorolling and subsequent aging

Tensile Behavior and Microstructure Evolution of an Extruded 6082 Aluminum Alloy Sheet at High Temperatures

Damage Mechanisms of 2195-O Aluminum Alloy Sheet Induced by Microstructural Evolution During Tensile Deformation at Different Temperatures