Low-temperature architecture of a cubic-phase CsPbBr 3 single crystal for ultrasensitive weak-light photodetectors

Xiangfeng Wei,Han Liu,Zhixiang Zhang,Wenchao Xu,Wenjun Huang,Lin-Bao Luo,Jiehua Liu
DOI: https://doi.org/10.1039/d1cc03460j
IF: 4.9
2021-01-01
Chemical Communications
Abstract:Cubic-phase CsPbBr 3 single crystals are synthesized by regulating H 2 O with CsBr/PbBr 2 in a ratio of 1 : 1 at low temperature by the freezing method. The CsPbBr 3 single-crystal photodetector exhibits a superior weak-light responsivity of 278 A W −1 .
chemistry, multidisciplinary
What problem does this paper attempt to address?
The problem that this paper attempts to solve is how to synthesize cubic - phase CsPbBr₃ single crystals at low temperatures and apply them to ultrasensitive low - light photodetectors. Specifically, the authors successfully synthesized cubic - phase CsPbBr₃ single crystals that are stable at low temperatures through the water - regulation method. This material has high responsivity, high external quantum efficiency, and high detectivity, and is particularly suitable for low - light detection under low - power 520 - nm light irradiation. ### Background and Problems 1. **Material Characteristics** - CsPbBr₃ is an all - inorganic perovskite material with a high light - absorption coefficient, a long carrier - transport distance, and fewer defects. These characteristics make it perform well in optoelectronic devices. - Compared with the orthorhombic and tetragonal phases, the cubic - phase CsPbBr₃ has smaller lattice parameters and higher stability. 2. **Existing Challenges** - Most reported CsPbBr₃ single crystals have an orthorhombic - phase structure at room temperature. - When preparing CsPbBr₃ single crystals using the traditional solvent method, due to the different saturated solubilities of CsBr and PbBr₂ in the solvent, it is easy to cause the formation of impurity phases. - Under high - temperature conditions, the surface energy of cubic - phase CsPbBr₃ is high, which is not conducive to the growth of single crystals. ### Solutions 1. **Water - Regulation Method** - By adding an appropriate amount of water to the DMSO solution to adjust the saturated solubilities of CsBr and PbBr₂ to be close to or equal, thereby promoting the growth of cubic - phase CsPbBr₃ single crystals. - Experiments have found that at 45°C, adding 38.1 wt% of water can achieve a 1:1 molar ratio of CsBr and PbBr₂ and successfully synthesize cubic - phase CsPbBr₃ single crystals. 2. **Optoelectronic Properties** - A photodetector based on cubic - phase CsPbBr₃ single crystals was prepared. The test results show that it has an ultra - high responsivity (278 A/W), external quantum efficiency (6.63 × 10⁴%), and detectivity (4.36 × 10¹³ Jones) under low - power 520 - nm light irradiation. - These performance indicators show that cubic - phase CsPbBr₃ single crystals have significant advantages in low - light detection. ### Conclusion The low - temperature - stable cubic - phase CsPbBr₃ single crystals were successfully synthesized through the water - regulation method, and their excellent performance in ultrasensitive low - light photodetectors was demonstrated. This method provides a new approach for preparing high - performance inorganic perovskite single crystals.