Ag2O@UiO-66 new thin film as p–n heterojunction: permanent photoreduction of hexavalent Cr

Sara Amiri,Mohammad Chahkandi,Mahboobeh Zargazi

DOI: https://doi.org/10.1039/d3ra06305d

IF: 4.036

2024-01-26

RSC Advances

Abstract:The new nanosphere Ag 2 O@UiO-66 thin-film was synthesized on a stainless steel mesh surface via an electrophoretic deposition method, and is used as an effective and low-cost photocatalyst using visible light. The synthesized nanocomposite was used to perform photo-reduction of Cr( VI ) ions under white light irradiation. The best removal rate (72% after 15 minutes) was obtained by the film with 0.034 grams of deposited composite having relative percentages of Ag 2 O : UiO-66 of 70 : 30. The interesting obtained results confirm that the p–n heterojunction of the composite is the main cause of the desired charge separation and the photoreduction speed increase. In the following, the resulting compounds were characterized by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), transmittance electron microscopy (TEM), field emission scanning electron microscopy (FE-SEM), energy diffraction X-ray spectroscopy (EDAX) and the Brunauer, Emmett, and Teller (BET) method. Scavenging studies performed in the presence of familiar scavengers confirmed that superoxide radicals ( ̇O 2 − ) and dissolved oxygen gas have a significant role in the photocatalytic reduction process.

chemistry, multidisciplinary

What problem does this paper attempt to address?

The paper aims to address the issue of hexavalent chromium (Cr(VI)) pollution. Specifically, the research team synthesized a new nano-composite film material—Ag₂O@UiO-66, and used it as a photocatalyst to photoreduce toxic hexavalent chromium in aqueous solutions to the less toxic trivalent chromium (Cr(III)) under visible light irradiation. The main goal of the study is to develop an efficient, low-cost, and environmentally friendly method to treat hexavalent chromium pollution in industrial wastewater.

The specific issues addressed in the paper are as follows:
1. **Development of a new photocatalyst**: Ag₂O@UiO-66 nano-composite film was synthesized on a stainless steel mesh via electrophoretic deposition for the photocatalytic reduction of hexavalent chromium.
2. **Improving photocatalytic efficiency**: The photocatalytic performance of composite materials with different ratios of Ag₂O and UiO-66 was studied, and it was found that the composite material with a 70:30 ratio had the best photocatalytic reduction effect.
3. **Verification of the role of active species**: By adding common scavengers (such as ethanol, isopropanol, sodium iodate, and sodium azide), the role of different active species (such as superoxide radicals and dissolved oxygen) in the photocatalytic process was investigated.
4. **Evaluation of material stability and reusability**: The photocatalytic performance of the Ag₂O@UiO-66 film was tested after multiple cycles of use, and the results showed good stability and reusability.
5. **Optimization of film thickness**: By changing the weight of the deposited composite material, the optimal photocatalytic reduction effect (72% within 15 minutes) was found.

In summary, the paper is mainly dedicated to developing an efficient photocatalytic material to address the issue of hexavalent chromium pollution in the environment.