Thermally Stable RuO x –CeO 2 Nanofiber Catalysts for Low-Temperature CO Oxidation
Zhongqi Liu,Yang Lu,Matthew P. Confer,Hao Cui,Junhao Li,Yudong Li,Yifan Wang,Shane C. Street,Evan K. Wujcik,Ruigang Wang
DOI: https://doi.org/10.1021/acsanm.0c01815
IF: 6.14
2020-07-23
ACS Applied Nano Materials
Abstract:With the ever-growing concerns for sustainable energy production and clean air, developing highly efficient catalysts to eliminate exhaust emission pollutants is of vital importance. In this work, we report a class of thermally stable RuO<i><sub>x</sub></i>–CeO<sub>2</sub> nanofiber catalysts derived from a facile one-pot electrospinning method. Ru–CeO<sub>2</sub> nanofiber catalysts exhibit outstanding low-temperature activity (∼90% conversion of CO below 150 °C) and long-term durability. The as-prepared Ru–CeO<sub>2</sub> nanofiber catalysts show a high Brunauer–Emmett–Teller (BET) surface area (>110 m<sup>2</sup>/g), demonstrating the effectiveness of electrospinning for fabricating high-surface-area catalysts. The Ru–CeO<sub>2</sub> nanofiber catalysts have a hollow interior and porous exterior structure, particularly at the Ru–CeO<sub>2</sub> nanofiber interfaces, providing plentiful accessible CO and oxygen adsorption sites, which are beneficial for CO catalytic oxidation. H<sub>2</sub> temperature-programmed reduction (H<sub>2</sub>-TPR) was applied to probe the reducibility of the as-synthesized catalysts. The reduced Ru–CeO<sub>2</sub> nanofiber catalysts exhibited hydrogen consumption near room temperature. The catalysts were further characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and transmission electron microscopy (TEM) to explore the relationship between the microstructure and extraordinary low-temperature reducibility, as well as the CO oxidation activity. In addition, X-ray photoelectron spectroscopy (XPS), in situ CO-diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS), and density functional theory (DFT) calculation were employed to investigate the chemical states of the active surface species and identify the gas adsorption and reaction sites.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.0c01815?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.0c01815</a>.Optimized Ru–CeO<sub>2</sub>(111) Cartesian coordinates in Angstroms; DOS of pure Ru–CeO<sub>2</sub>(111) and repaired Ru–CeO<sub>2</sub>(111); adsorption configurations for the Ru–CeO<sub>2</sub>(111)/CO system, Ru–CeO<sub>2</sub>(111)/O<sub>2</sub> system, CeO<sub>2</sub>(111)/CO system, and CeO<sub>2</sub>(111)/ O<sub>2</sub> system; TGA curves of Ce(NO<sub>3</sub>)<sub>3</sub>·6H<sub>2</sub>O, PVP (<i>M</i><sub>w</sub> = 1 300 000), and electrospun Ce(NO<sub>3</sub>)<sub>3</sub>/PVP precursor fibers (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.0c01815/suppl_file/an0c01815_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology