Abstract:This study prepared silicon oxide anode materials with nitrogen-doped carbon matrices (SiOx/C–N) through silicon-containing polyester thermal carbonization. Melamine was introduced as a nitrogen source during the experiment. This nitrogen doping process resulted in a porous structure in the carbon matrices, a fact confirmed by scanning electron microscopy (SEM). Pyridinic and quaternary nitrogen, but mainly tertiary nitrogen, were generated, as shown via X-ray photoelectron spectroscopy (XPS). Electrochemical tests confirmed that, as anode materials for a lithium-ion battery, SiOx/C–N provided better cycle stability, improved rate capability, and lower Li+ diffusion resistance. The best performance showed an activated capacity at 493.5 mAh/g, preserved at 432.8 mAh/g after the 100th cycle, with 87.7% total Columbic efficiency. Those without nitrogen doping gave 1126.7 mAh/g, 249.0 mAh/g, and 22.1%, respectively. The most noteworthy point was that, after 100 cycles, anodes without nitrogen doping were pulverized into fine powders (SEM); meanwhile, in the case of anodes with nitrogen doping, powders of a larger size (0.5–1.0 μm) formed, with the accumulation of surrounding cavities. We suggest that the formation of more prominent powders may have resulted from the more substantial nitrogen-doped carbon matrices, which prevented the anode from further breaking down to a smaller size. The volume expansion stress decreased when the powders decreased to nanosize, which is why the nanosized silicon anode materials showed better cycling stability. When the anodes were cracked into powders with a determined diameter, the stress from volume expansion decreased to a level at which the powders could preserve their shape, and the breakage of the powders was stopped. Hence, the diameters of the final reserved powders are contingent on the strength of the matrix. As reported, nitrogen-doped carbon matrices are more robust than those not doped with nitrogen. Thus, in our research, anodes with nitrogen-doped carbon matrices presented more large-diameter powders, as SEM confirmed. Anodes with nitrogen doping will not be further broken at a larger diameter. At this point, the SEI film will not show continuous breakage and formation compared to the anode without doping. This was validated by the lower deposition content of the SEI-film-related elements (phosphorous and fluorine) in the cycled anodes with nitrogen doping. The anode without nitrogen doping presented higher content, meaning that the SEI films were broken many times during lithiation/delithiation (EDS mapping).

Nitrogen and Oxygen Dual‐Doped Carbon as High‐Rate Long‐Cycle‐Life Anode Materials for Lithium‐Ion Batteries

In Situ Nitrogen-Doped Helical Mesoporous Carbonaceous Nanotubes for Superior-High Lithium Anodic Performance

Nitrogen self-doped carbon with super high-rate and long cycle life as anode materials for lithium-ion batteries

Nitrogen-doped 3D nanocarbon with nanopore defects as high-capacity and stable anode materials for sodium/lithium-ion batteries

Lignin-Derived Nitrogen-Doped Porous Carbon as a High-Rate Anode Material for Sodium Ion Batteries

Nitrogen Doped Porous Carbon with High Rate Performance for Lithium Ion Storage

Nitrogen-Doped Carbon Nanocages As High-Rate Anode for Lithium Ion Batteries

Nitrogen and Phosphorus Codoped Porous Carbon Framework As Anode Material for High Rate Lithium-Ion Batteries

Balance between favored activity and side reactions of nitrogen doped carbon as cathode material in Lithium-oxygen battery

High‐Level Pyridinic‐N‐Doped Carbon Nanosheets with Promising Performances Severed as Li‐Ion Battery Anodes

Expandable nitrogen-doped carbon-based anodes fabricated from self-sacrificial metal-organic frameworks for ultralong-life lithium storage

Nitrogen and Oxygen Codoped Carbon Anode Fabricated Facilely from Polyaniline Coated Cellulose Nanocrystals for High-Performance Li-Ion Batteries

High Lithium Anodic Performance of Highly Nitrogen-Doped Porous Carbon Prepared from a Metal-Organic Framework

High stability and high performance nitrogen doped carbon containers for lithium-ion batteries.

N-doped catalytic graphitized hard carbon for high-performance lithium/sodium-ion batteries

Nitrogen-Doped Carbon-Coating Disproportionated SiO Materials As Long Cycling Stable Anode for Lithium Ion Batteries

Nitrogen-Doped Hollow Carbon Nanospheres for High-Performance Li-Ion Batteries.

Hierarchical Self-Supported Carbon Nanostructure Enables Superior Stability of Highly Nitrogen-Doped anodes

Nitrogen-Doped Carbon Matrix to Optimize Cycling Stability of Lithium Ion Battery Anode from SiOx Materials

Nitrogen Dual-Doped Porous Carbon Fiber: A Binder-Free and High-Performance Flexible Anode for Lithium Ion Batteries

Carbon Electrode with NiO and RuO2 Nanoparticles Improves the Cycling Life of Non-Aqueous Lithium-Oxygen Batteries