Room-temperature ferromagnetism enhancement in Fe-doped VSe2 nanosheets synthesized by a chemical method

Li-Yan Hu,Li-Fang Yu,Huan Yang,Xian Xu,Fang Wang,Xiao-Hong Xu

DOI: https://doi.org/10.1007/s12598-021-01740-1

IF: 6.318

2021-04-24

Rare Metals

Abstract:<p class="a-plus-plus">Two-dimensional (2D) few-layer VSe<sub class="a-plus-plus">2</sub>, V<sub class="a-plus-plus">1−<em class="a-plus-plus">x</em></sub>Fe<sub class="a-plus-plus"><em class="a-plus-plus">x</em></sub>Se<sub class="a-plus-plus">2</sub> nanosheets have been synthesized by a high-temperature organic solution-phase method. The thickness of VSe<sub class="a-plus-plus">2</sub> nanosheets can be tuned from 12 to 5 layers by decreasing the precursor concentrations. The few-layer VSe<sub class="a-plus-plus">2</sub> nanosheets show the room-temperature ferromagnetism. The coercivity and magnetization reach 0.024 T and 0.036 mA·m<sup class="a-plus-plus">2</sup>·g<sup class="a-plus-plus">−1</sup> at room temperature. The charge-density wave behavior is also confirmed in VSe<sub class="a-plus-plus">2</sub> by the hysteresis loops and zero-field-cooling curve. V<sub class="a-plus-plus">1−<em class="a-plus-plus">x</em></sub>Fe<sub class="a-plus-plus"><em class="a-plus-plus">x</em></sub>Se<sub class="a-plus-plus">2</sub> nanosheets can be obtained by doping Fe(acac)<sub class="a-plus-plus">3</sub> in the reaction process. The room-temperature coercivity and magnetization of V<sub class="a-plus-plus">0.8</sub>Fe<sub class="a-plus-plus">0.2</sub>Se<sub class="a-plus-plus">2</sub> nanosheets are 5 times higher than those of the pure VSe<sub class="a-plus-plus">2</sub> nanosheets without destroying the structures. The enhancement of magnetization is due to the coupling interaction of 3d orbits between V and Fe atoms. Higher Fe concentration is beneficial to improve the coercivity, which is attributed to the formation of the second phase Fe<sub class="a-plus-plus">3</sub>Se<sub class="a-plus-plus">4</sub>. This simple chemical preparation method can be extended to prepare the other 2D materials.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering