Mechanism of microarc oxidation on AZ91D Mg alloy induced by β-Mg17Al12 phase
Dajun Zhai,Xiaoping Li,Jun Shen
DOI: https://doi.org/10.1007/s12613-023-2752-0
2024-04-18
International Journal of Minerals Metallurgy and Materials
Abstract:This work proposed a strategy of indirectly inducing uniform microarc discharge by controlling the content and distribution of β-Mg 17 Al 12 phase in AZ91D Mg alloy. Two kinds of nano-particles (ZrO 2 and TiO 2 ) were designed to be added into the substrate of Mg alloy by friction stir processing (FSP). Then, Mg alloy sample designed with different precipitated morphology of β-Mg 17 Al 12 phase was treated by microarc oxidation (MAO) in Na 3 PO 4 /Na 2 SiO 3 electrolyte. The characteristics and performance of the MAO coating was analyzed using scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), contact angle meter, and potentiodynamic polarization. It was found that the coarse α-Mg grains in extruded AZ91D Mg alloy were refined by FSP, and the β-Mg 17 Al 12 phase with reticular structure was broken and dispersed. The nano-ZrO 2 particles were pinned at the grain boundary by FSP, which refined the α-Mg grain and promoted the precipitation of β-Mg 17 Al 12 phase in grains. It effectively inhibited the "cascade" phenomenon of microarcs, which induced the uniform distribution of discharge pores. The MAO coating on Zr-FSP sample had good wettability and corrosion resistance. However, TiO 2 particles were hardly detected in the coating on Ti-FSP sample.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing