Electro-adsorption of Cs(I) ions from aqueous solution by capacitive deionization using ACC/MoO 3 composite electrode

Xiaojing Liu,Jinling Wu,Jianlong Wang

DOI: https://doi.org/10.1016/j.scitotenv.2022.161110

2022-12-31

Abstract:The separation of Cs + from radioactive wastes is of paramount importance, but still a challenge. In this paper, ACC/MoO 3 composite electrode was prepared and used for the separation of Cs + by capacitive deionization (CDI). The electrode materials were characterized by SEM-EDS, FTIR, XPS before and after adsorption experiments. The composite electrode was composed of ACC and hexagonal tunnel structure of MoO 3 , which had a mesoporous structure. The specific surface area, average pore diameter, total pore volume and maximal specific capacitance were 170.4 m 2 g −1 , 2.127 nm, 0.906 cm 3 g −1 and 76.3 F g −1 , respectively. The adsorption kinetics, isotherms, and the mass transfer process were analyzed, and the possible adsorption mechanism was proposed. The removal efficiency of Cs + increased with the increase of voltage and the decrease of Cs + concentration, which reached 44.7 % after 240 min when voltage was 1.2 V and Cs + concentration was 5 mg L −1 . The Cs + adsorption onto the ACC/MoO 3 composite was multi-layer adsorption and the adsorption to active sites (AAS) was the rate-limiting step. Overall, the ACC/MoO 3 composite was a potential electrode for Cs + separation.

environmental sciences