Multi-Interface-Induced Thermal Conductivity Reduction and Thermoelectric Performance Improvement in a Cu–Ni Alloy
Chuang Jia,Xiao Xu,LiJie Zhong,DingXuan Kang,Peng Shen,Biao Xu,Jing Bai,Feng Xue,Kang Yin,BeiBei Zhu,Li Tao
DOI: https://doi.org/10.1021/acsaem.2c00404
IF: 6.4
2022-04-04
ACS Applied Energy Materials
Abstract:A Cu–Ni-based alloy with a high power factor is a commercially utilized metallic thermocouple material. However, the high thermal conductivity has been a major limitation to achieving thermoelectric performance in semiconductor materials. Herein, this work presents a 76.1% reduced thermal conductivity (∼7.7 W m–1 K–1) in Cu70Ni30, which is one of the lowest reported values in the literature. Such suppression of thermal conductivity can be attributed to the varied frequency phonon scattering by the interfacial potential barrier, built from micron-scale defects formed via sintering melt-spun ribbons. However, the defects simultaneously reduce the charge carrier concentration, mobility, and thus the electrical conductivity. The lowest thermal conductivity leads to the highest zT and ZTavg in the sample sintered at 673 K under 15 MPa. The values are 0.24 (@573 K) and 0.15 (323–573 K), respectively, which are 130.3 and 140.0% higher than the values of the pristine counterpart. Our work demonstrates that improved thermoelectric performance in Cu–Ni-based alloys can be obtained by creating various interfacial defects even at micron scales, which paves the way to suppress thermal conductivity largely in metallic thermoelectric materials via melt-spinning (MS) and spark plasma sintering (SPS) synthesis.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.2c00404.Additional EDS mapping images, SEM images, calculated κl and κe of Cu70Ni30-sintered bulks according to the Wiedemann–Franz law, fitting values a and b in eq 2, κl/κT of sintered bulks at 323 and 573 K, and Pisarenko plots (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels