Controlled Atmosphere Corrosion Engineering toward Inhomogeneous NiFe-LDH for Energetic Oxygen Evolution

Shichao Du,Zhiyu Ren,Xiaolei Wang,Jun Wu,Huiyuan Meng,Honggang Fu
DOI: https://doi.org/10.1021/acsnano.2c00332
IF: 17.1
2022-04-18
ACS Nano
Abstract:The "Fe effect" can maximize the activity of nickel-iron layered double hydroxides (NiFe-LDH) toward oxygen evolution reaction (OER) when the iron content, the lattice distortion, the conductivity, and other related factors are well balanced. It is difficult for the homogeneous NiFe-LDH to take good care of the above requirements at the same time. Herein, we proposed an elaborate atmosphere corrosion strategy to construct porous NiFe-LDH with rich edge/surface-Fe defects on Ni foam (NF). Such edge/surface-Fe defects, mainly caused by the local unequal-stoichiometric ratio of Fe/Ni in the nanometer or subnanometer region, are determined by the unbalanced permeating of the acid vapor and the confined reaction of local Fe and Ni species ionized by the acid vapor. Benefiting from the abundant and fantastic edge/surface-Fe defects, the optimal NiFe-LDH prepared by atmosphere corrosion is more energetic for OER than that synthesized in conventional liquid phase, only a potential of 1.481 and 1.552 V<sub>RHE</sub> to respectively achieve the current density of 100 and 1000 mA cm<sup>-2</sup> as well as a satisfactory stability and reproducibility. An overall water-splitting system assembled by inhomogeneous NiFe-LDH and commercial Pt-C can reach a current density of 100 mA cm<sup>-2</sup> at a solar cell of 1.72 V. Additionally, the atmosphere corrosion is very suitable for the large-scale, green, and economic synthesis of metal-based catalysts with high enrichment of defects, highlighting its potential for device and industrial applications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology
What problem does this paper attempt to address?
The key problem that this paper attempts to solve is to improve the catalytic activity and stability of nickel - iron layered double hydroxides (NiFe - LDH) in the oxygen evolution reaction (OER), especially maintaining these properties during large - scale preparation. Specifically, the authors aim to construct a heterogeneous NiFe - LDH array with abundant edge/surface iron defects on nickel foam (NF) through a carefully designed atmospheric corrosion strategy, thereby breaking through the bottleneck of traditional homogeneous NiFe - LDH catalysts in OER activity. ### Main problems and solutions 1. **Improvement of OER activity**: - **Background problem**: Traditional homogeneous NiFe - LDH is difficult to meet the requirements of high Fe content, appropriate lattice distortion, good conductivity, etc. simultaneously, resulting in limited OER activity. - **Solution**: A heterogeneous NiFe - LDH with abundant edge/surface iron defects is constructed on nickel foam through the atmospheric corrosion method. These defects make the catalyst show higher activity in OER. 2. **Large - scale green synthesis**: - **Background problem**: Existing liquid - phase synthesis methods are not conducive to large - scale production and may generate waste liquid, which does not meet the requirements of green chemistry. - **Solution**: The proposed atmospheric corrosion strategy is not only suitable for large - scale production but also environmentally friendly. There is no need to deal with waste liquid, and energy consumption is reduced. 3. **Stability and reproducibility**: - **Background problem**: The stability and reproducibility of the catalyst during long - term use are key challenges in practical applications. - **Solution**: By optimizing the atmospheric corrosion conditions, the stability and reproducibility of the catalyst in structural characteristics and catalytic activity are ensured. ### Experimental results - **OER performance**: The overpotentials of the optimal A - NiFe/NF electrode at current densities of 100 mA cm\(^{-2}\) and 1000 mA cm\(^{-2}\) are 251 mV and 322 mV respectively, which are significantly better than other catalysts. - **Stability**: After 75 hours of OER testing, A - NiFe/NF can still maintain an overpotential of about 332 mV, and the LSV curve is basically the same as the initial state. - **Large - scale preparation**: An A - NiFe/NF electrode with a size of 20.0 cm × 24.0 cm has been successfully prepared, verifying the large - scale feasibility of this method. In conclusion, this research solves the problems of activity, stability, and large - scale green synthesis of NiFe - LDH in OER through an innovative atmospheric corrosion strategy, providing new ideas for the development of efficient water - splitting systems.