Preparation and characterization of highly conductive lignin aerogel based on tunicate nanocellulose framework
Weijie Lin,Shuai Wu,Shibo Han,Jie Xie,Hongshen He,Qiuxia Zou,Dezhong Xu,Dengwen Ning,Ajoy Kanti Mondal,Fang Huang
DOI: https://doi.org/10.1016/j.ijbiomac.2023.125010
IF: 8.2
2023-06-03
International Journal of Biological Macromolecules
Abstract:The highly conductive and elastic three-dimensional mesh porous material is an ideal platform for the fabrication of high electrical conductivity conductive aerogels. Herein, a multifunctional aerogel that is lightweight, highly conductive and stable sensing properties is reported. Tunicate nanocellulose (TCNCs) with a high aspect ratio, high Young's modulus, high crystallinity, good biocompatibility and biodegradability was used as the basic skeleton to prepare aerogel by freeze-drying technique. Alkali lignin (AL) was used as the raw material, polyethylene glycol diglycidyl ether (PEGDGE) was used as the cross-linking agent, and polyaniline (PANI) was used as the conductive polymer. Preparation of aerogels by freeze-drying technique, in situ synthesis of PANI, and construction of highly conductive aerogel from lignin/TCNCs. The structure, morphology and crystallinity of the aerogel were characterized by FT-IR, SEM, and XRD. The results show that the aerogel has good conductivity (as high as 5.41 S/m) and excellent sensing performance. When the aerogel was assembled as a supercapacitor, the maximum specific capacitance can reach 772 mF/cm 2 at 1 mA/cm 2 current density, and maximum power and energy density can reach 59.4 μWh/cm 2 and 3600 μW/cm 2 , respectively. It is expected the aerogel can be applied in the field of wearable devices and electronic skin.
polymer science,biochemistry & molecular biology,chemistry, applied