Monolithic flexible supercapacitors drawn with nitrogen-doped carbon nanotube-graphene ink

Sheng Zhu,Jian Sheng,Guodong Jia,Zeyao Zhang,Jia Guo,Meng Wang,Jiangfeng Ni,Yan Li

DOI: https://doi.org/10.1016/j.materresbull.2021.111266

IF: 5.6

2021-07-01

Materials Research Bulletin

Abstract:<p>We demonstrate a facile strategy to fabricate flexible paper-based supercapacitors, in which all the components are integrated onto a paper with poly (vinyl alcohol)/H₃PO₄ as the gel electrolyte. The electrodes are drawn on both sides of the paper in a mirror image with a surfactant-free ink of nitrogen-doped carbon nanotubes and graphene. The resultant supercapacitors present a high volumetric capacitance of 0.45 F cm⁻³ and an energy density of 40.0 μWh cm⁻³. Moreover, this strategy is intrinsically scalable toward flexible energy devices while maintaining their electrochemical and mechanical performance.</p>

materials science, multidisciplinary

What problem does this paper attempt to address?

The paper mainly addresses the following issues:

1. **Developed a simple strategy to prepare flexible paper-based supercapacitors**: By integrating all components (including electrodes, separators, current collectors, etc.) on paper, and using polyvinyl alcohol/phosphoric acid hydrogel as the electrolyte, as well as surfactant-free ink of nitrogen-doped carbon nanotubes and graphene as electrode materials.

2. **Achieved good dispersion of electrode materials**: Utilizing graphene as a dispersant to solve the problem of carbon nanotubes being difficult to disperse in solvents, and carbon nanotubes can also prevent the overlapping of graphene nanosheets, forming a stable ink.

3. **Improved energy density and volumetric capacitance**: By drawing the electrodes on both sides of the paper, the entire volume of the device is fully utilized, thereby improving the energy density and volumetric capacitance (reaching 40.0 μWh/cm³ and 0.45 F/cm³, respectively).

4. **Enhanced mechanical performance**: The prepared flexible paper-based supercapacitor has good flexibility and stability, maintaining a high capacitance value even after multiple bends (after 200 cycles of bending from 0° to 180°, the capacitance retention rate is 92.9%).

5. **Achieved large-scale production**: Successfully scaled up the supercapacitor using a simple dip-coating process, indicating that this method has the potential for simplicity, scalability, and mass production.

In summary, this research proposes a novel method to manufacture high-performance, flexible, and easily scalable paper-based supercapacitors, providing a new solution for energy storage in future miniaturized electronic devices.