Abstract:Sr3YCo4O10.5+δ (314-SYCO), with an unusual ordered structure and a high Curie temperature (Tc ≈ 335 K), is attracting increasing attention. Herein, to improve the electrical performance of 314-SYCO, Cu-doped Sr3YCo4-x Cu x O10.5+δ (x = 0-0.8) ceramics were prepared using a solid-state reaction method. Systematic research was conducted on both the ordered phase transformation and the effects of Cu doping on the microstructure, electrical transport characteristics, and magnetic properties. For x = 0-0.4, the (103) and (215) planes were observed and combined with Rietveld refinement results for the X-ray diffraction data, confirming the formation of ordered tetragonal Sr3YCo4-x Cu x O10.5+δ . This phase was formed with a mass gain of ∼0.8% and heat released at ∼1,042°C. With increasing Cu content, the concentration of hole carriers also increased, leading to a substantial reduction in electrical resistivity. The electrical resistivity decreased by 92-99% at 300 K. The polycrystalline materials have semiconducting behaviour with a three-dimensional Mott variable-range hopping mechanism. For the magnetic properties, a Hopkinson peak was observed at 319 K, and the Tc was approximately 321 K for x = 0. The magnetisation and Tc decreased with increasing Cu content, and a G-type antiferromagnetic-to-ferromagnetic phase transition occurred due to the spin state change for some Co3+ ions from high/intermediate spin to low/intermediate spin. These results lay the groundwork for refinement of the sintering procedure and doping parameters to enhance the performance of 314-SYCO in the context of current applications such as microwave absorbers and solid oxide fuel cell cathodes.

Charge and spin degrees of freedom in A -site ordered Y Cu 3 Co 4 O 12 and Ca Cu 3 Co 4 O 12

Cobalt Substitution Effects in the Spin Ladder Compound Sr14-Xcaxcu24-Ycoyo41

Structure, Phonon Vibration, and Spin Correlation of LaBa2Cu3−x Co X O Y

Tunable Interplay Between 3d and 4 F Electrons in Co-Doped Iron Pnictides

Compensation Effect of Substitutions at Cu(1) and Y-Sites on Superconductivity in the Yba2cu3o6.5+Z System

DOPING EFFECTS IN YBa2Cu1-xCox(Cu1-yZny)2Oz SYSTEM

Prevailing Charge Order in Overdoped La<sub>2-<i>x</i></sub>Sr<i><sub>x</sub></i>CuO<sub>4</sub> beyond the Superconducting Dome

Prevailing Charge Order in Overdoped La_{2-x}Sr_{x}CuO_{4} beyond the Superconducting Dome.

Prevailing Charge Order in Overdoped La2-1Sr1CuO4 beyond the Superconducting Dome

Mechanisms Of Substitution Effects On Different Lattice Sites In Yba2cu3o7-Y

EFFECT OF THE LOCAL SUBSTITUTION OF Co FOR Cu(1) ON THE ELECTRONIC STRUCTURE OF <font>YBa</font><sub>2</sub><font>Cu</font><sub>3</sub><font>O</font><sub>7</sub>

Spin and charge orders and their hole-doping dependence in single layered cobaltate La2-xCaxCoO4(0.3<x<0.8)

Single-crystal growth and dependences on the hole concentration and magnetic field of the magnetic ground state in the edge-sharing CuO$_2$ chain system Ca$_{2+x}$Y$_{2-x}$Cu$_5$O$_{10}$

Spin States Of The Co Ion In Charge-Ordered Ybaco2o5

Electronic structure of ( = Y, La, Bi): Synthesis, characterization, core-level spectroscopies, high-pressure application, and ab initio calculation

Stabilization of three-dimensional charge order in YBa$_2$Cu$_3$O$_{6+x}$ via epitaxial growth

High-Spin And Charge-Ordering State Of Ybaco2o5

Ordered phase transformation and Cu doping effects in room-temperature ferromagnetic Sr3YCo4O10.5+ δ

Structure and Spin-Gap in the Normal State of Y1−xCaxBa1.9Nd0.1Cu3Oy Cuprates

Magnetic and charge transport properties in underdoped YBa2Cu3O6+x and YBa2Cu4O8