Abstract:Zn modified ZSM-5 zeolite supported Ni bifunctional catalysts were prepared by in-situ hydrothermal synthesis (Zn-Ni-ZSM-5), co-impregnation method (Zn-Ni/ZSM-5) as well as combining in-situ hydrothermal synthesis of Zn-ZSM-5 and sequential impregnation of Ni (Ni/Zn-ZSM-5) and used for the selective converting olefin to aromatics applicable for FCC gasoline hydro-upgrading. The Lewis (L) acid sites generated by ZnOH+ species and hydrogenation active sites from Ni0 species were varied with preparation method, in which their locations at the external surface or micropores of zeolite changed the acid properties of catalysts. Comparing to the Zn-Ni/ZSM-5 from the co-impregnation method, direct in-situ hydrothermal method could incorporate Zn and Ni species within zeolite, which makes the strong interaction between the metal species and the framework Al to form medium-strong L acids (ZnOH+/NiOH+). This leads to the decrease of ratio of Brønsted acid sites to L acid sites (B/L) from 0.40 to 0.12 and the difficulty in reducing of Ni cations to Ni0 from 57% to 30% Ni0 percent. Ni/Zn-ZSM-5 sample prepared by incorporating Zn species into micropores and sequential depositing Ni species at the external surface of zeolite possesses a low B/L ratio similar to Zn-Ni-ZSM-5 (0.20 versus 0.12) but a much higher Ni0 percent (52% versus 30%). Zn-Ni-ZSM-5 shows closer intimacy between Zn and Ni species comparing to Zn-Ni/ZSM-5 and Ni/Zn-ZSM-5. For the 1-hexene aromatization, the formed iso-alkene at acid sites was quickly saturated to iso-alkanes by the adjacent Ni0 particles over Ni-Zn-ZSM-5 catalyst in hydrogen steam. However, the location of aromatization active sites (ZnOH+, L acid sites) in micropores and hydrogenation active sites (Ni0 species) on external surface of Ni/Zn-ZSM-5 makes the tandem conversion of n-alkene → iso-alkene → aromatics, rather than the n-alkene → iso-alkene → iso-alkane. Thus, Zn-Ni-ZSM-5 with close intimacy of ZnOH+ and Ni0 particles shows a high iso-alkane selectivity (27.9% iC4 +), while Ni/Zn-ZSM-5 exhibits a high aromatics selectivity (39.6 %) in the conversion of 1-hexene in hydrogen steam. Similar results have also found in the conversion of n-heptane. Here, the control of the intimacy of Zn and Ni in ZSM-5 zeolites has been realized to be a good protocol to adjust the selective conversion of olefins/alkanes to aromatics versus iso-alkanes.

Excellent Activity of Nb in Promoting Performance of ZSM-5–USY for the Catalytic Cracking of n-Hexane to Light Olefins

Al-Sn Bimetallic ZSM-5: Acidity Regulation and Excellent Performance in Cracking N-Hexane for Production of Light Olefins

Effect of Hierarchical ZSM-5 Zeolite Crystal Size on Diffusion and Catalytic Performance of N-Heptane Cracking

ZSM-5@MCM-41 core–shell composite with tunable shell thickness for n -heptane catalytic cracking reaction

Transition metal modified hierarchical ZSM-5 nanosheet for catalytic cracking of n -pentane to light olefins

ZSM–5@KIT–6 encapsulated composite molecular sieves for the catalytic cracking of waste cooking oil model compound to produce light olefins

Effects of post treatment of HZSM-5 zeolites on catalytic cracking of butene

Hierarchical ZSM-5 zeolite designed by combining desilication and dealumination with related study of n-heptane cracking performance

Preparation of nano ZSM-5 with hydrophobic surfaces and application to catalytic cracking of hydrocarbon fuels

Catalytic Cracking of N-Hexane to Light Alkene over ZSM-5 Zeolite: Influence of Hierarchical Porosity and Acid Property

Synthesis of Nanoscale ZSM-5 Zeolites for the Catalytic Cracking of Oleic Acid into Light Olefins and Aromatics

Strategies To Enhance The Catalytic Performance Of Zsm-5 Zeolite In Hydrocarbon Cracking: A Review

Synthesis and Performance of Pillared HZSM-5 Nanosheet Zeolites for N-Decane Catalytic Cracking to Produce Light Olefins

Synergetic Regulation of the Microstructure and Acidity of HZSM-5/MCM-41 for Efficient Catalytic Cracking of n-Decane

Insight into Reaction Path and Mechanism of Catalytic Cracking of N-Hexane in HZSM-5 Zeolites

HZSM-5/MCM-41 composite molecular sieves for the catalytic cracking of endothermic hydrocarbon fuels: nano-ZSM-5 zeolites as the source

Catalytic pyrolysis performance of alkanes to light olefins over bifunctional ZSM-5 zeolites

A Nanocrystalline ZSM‐5 for the Catalytic Cracking of Waste Cooking Oil

Rational Screening of Transition Metal Single-Atom-Doped ZSM-5 Zeolite Catalyst for Naphtha Cracking from Microkinetic Analysis

HZSM-5 zeolite cross-linked with ultrathin siliceous layer for intensifying catalytic cracking and diffusion of n-butane

Synthesis and consequence of Zn modified ZSM-5 zeolite supported Ni catalyst for catalytic aromatization of olefin/paraffin