Plasma Electrolytic Polishing Process for Zr-based Metallic Glasses and Waste Liquor Treatment
Chengyong Wang,Zimin Tang,Feng Ding,Yu Huang,Tao Zhang,Lijuan Zhneg,Xuguang Zhu
DOI: https://doi.org/10.11933/j.issn.1007-9289.20221017002
2024-01-01
China surface engineering
Abstract:Zirconium-based bulk metallic glasses (BMGs) exhibit metal and glass properties, excellent mechanical performance, corrosion resistance, and good biocompatibility. Zr-based BMG is currently the only amorphous alloy that has been industrially produced as a structural component, and its surface quality is a key factor affecting its operational performance. Plasma electrolytic polishing, which requires low electrical conductivity, is suitable for intricate workpieces and does not have any adverse effects on multiphase alloys. Thus, this is an ideal polishing technology for Zr-based BMG structural components. This study aimed to investigate the effects of plasma electrolytic polishing on the surface quality of Zr58Cu15.46Ni12.74Al10.34Nb2.76Y0.5 BMGs and obtain the optimal process parameters and polishing quality to provide process guidance for plasma electrolytic polishing in the actual production of Zr-based BMGs. The effects of different process parameters, such as polishing time, ammonium sulfate concentration of the electrolyte, working voltage, initial temperature, immersion depth of the workpiece, and anode rack materials, on the polishing surface roughness were studied using single-factor experiments. Subsequently, based on the single-factor experiments, we conducted four orthogonally designed experiments, each with four factors and four levels, using the factors that were more influential on the surface quality. These experiments aimed to minimize the surface roughness after polishing. Range and variance analyses were conducted to study the influence of each polishing process parameter on the surface roughness during polishing and determine the primary and secondary order of influence indicators, and the optimal combination of process parameters was obtained. To address the issue of waste liquor pollution after polishing, the effects of chemical neutralization-coagulative precipitation process and ion-exchange resin method on treating the waste liquor generated after polishing Zr-based BMGs were studied. A combination technology was proposed to treat the waste liquor. The quality of the effluent based on its compliance with the "National Emission Standard for Electroplating Waste Liquor" (GB21900-2008) was measuring. The results showed that the surface roughness of the Zr-based BMGs decreased and stabilized with increasing polishing time. A working voltage that was too high or too low could notachieve good surface quality, and the lowest surface roughness was achieved at a working voltage of 210 V. Ammonium sulfate wasthe primary component of the electrolyte, and ammonium sulfate concentrations that were too high or too low could affect the polishing effect. A concentration of 4.5% resulted in the lowest surface roughness. As the initial temperature increases, the roughness of the polished surfaces decreases. The immersion depth of the workpiece affects its surface pressure, which in turn, affects the formation of the surface air layer, with excessive immersion depth increasing the surface roughness. Copper anode rack materials can achieve lower surface roughness than stainless-steel anode rack materials. The results of the orthogonal experiment with the minimum surface roughness as the objective showed that the significant degree of factors affecting the surface roughness after polishing were the polishing time, working voltage, initial temperature, and ammonium sulfate concentration. The optimal combination of polishing process parameters was achieved with a polishing time, a working voltage, an initial temperature, and an ammonium sulfate concentration of 8 min, 220 V, 88 degree celsius, and 5%, respectively. The optimal surface roughness obtained in the experiments was 0.103 mu m. The chemical neutralizing-coagulative precipitation process or ion-exchange resin method alone could not meet the "National Emission Standard for Electroplating Waste Liquor" through a single waste liquor treatment process. However, a combination of the two could effectively treat heavy metals and fluoride ions in the waste liquor generated after the polishing of Zr-based BMGs and reduce the concentration of heavy metals and fluoride ions in the effluent to meet the national standard for electroplating waste liquor. The research results will be helpful for promoting the industrial application of Zr-based BMG structural components and mass production and application of Zr-based BMGs