Dielectric and Mechanical Properties of Silicone Rubber Composites Reinforced by Conductive Carbon Black and Neopentyl Glycol Diglycidyl Ether
Vinayak Adimule,Shashanka Rajendrachari,Rayappa Mahale,Sheetal Batakurki,Basappa C Yallur,Santosh Nandi,Gangadhar Bagihalli
DOI: https://doi.org/10.1007/s12633-022-02210-8
IF: 3.4
2022-11-12
Silicon
Abstract:In the present investigation, dielectric, tensile strength, fracture toughness, and stress-strain properties of silicone rubber (SR) dispersed with carbon black (CB), and neopentyl glycol diglycidyl ether (NPGDE) (5 wt%, 10 wt%, and 12 wt%) were studied. Flake-like agglomerated morphology was confirmed from SEM (scanning electron microscope) studies as the CB@NPDGE filler concentration increases in the SR matrix. Surface area (354–358/cm 3 /g/A), pore size, and pore diameter (2.89 nm) remarkably increased for SR: CB@NPDGE polymer composites when compared with virgin SR. TGA spectra showed an increase in the decomposition temperature (600 °C) for SR: CB/NPDGE polymer composite when compared with virgin SR. A slight shift in the wavenumber of the functional groups resulted as the CB@NPDGE concentration increases in the SR polymer matrix. Optical absorbance shift towards the right side of the spectrum (redshift), broadened as CB@NPDGE concentration increased in SR polymer and optical band gap (E g ) decreases from 3.50 eV to 2.64 eV. SR:CB@NPDGE (10 wt% and 12 wt%) displayed improved dielectric properties having dielectric constant (1.68 × 10 3 , 4.87 × 10 3 ), dielectric permittivity (10 1 -10 3 /10 4 ), and dielectric loss (< 1.1/0.05) when compared with virgin SR. Significant improvements in the stress-strain and tensile strength properties resulted for SR:CB@NPDGE (10 wt% and 12 wt%) polymer composites. Compressive strength and tensile strength were found to be ~ 12.909 MPa and ~ 136.2 MPa. The peak load is between 0.254 kN to 1.907kN. The elongation at break for SR:CB@NPDGE (12 wt%) polymer composite was found to be 97.14% with 14.07 kN/mm of stiffness. An increase in temperature leads to an increase in dielectric permittivity and ac conductivity for different wt% of CB@NPDGE in SR polymer composites. Further, tensile strength, and tensile strain to failure decreases monotonically with an increase in temperature (100 °C). The present research gives a pathway for the development of organic hybrid polymer-reinforced composite structures for piezoelectric, dielectric, and structural applications.
materials science, multidisciplinary,chemistry, physical