Abstract:The effect of both the Fe : Ni ratio (5 to 1 : 1) and the relative Lewis acidity of a metal oxide support on catalytic activity, selectivity and stability was investigated in the CO2 mediated oxidative dehydrogenation of ethane (CO2-ODH). To avoid effects of varying pore sizes, shapes and volumes of the supports, chromia and zirconia overlayers were coated onto a common γ-Al2O3 carrier (CrOx@Al2O3 and ZrOx@Al2O3). Separately, oxidic FexNiy alloy precursor nanoparticles were prepared using a nonaqueous surfactant-free method and deposited by sonication onto the carrier. In comparison to previous studies in the field, this synthesis technique yields closely associated iron and nickel increasing the chances for alloy formation. During reduction, a mixture of a bcc and a fcc alloy phase was formed, with the content of bcc increasing with increasing iron content as predicted by the bulk phase diagram. Upon exposure to carbon dioxide at elevated temperatures, the bcc metallic phase is selectively oxidised to an inverse spinel structure via the dissociation of CO2. When exposed to CO2-ODH conditions, the bare ZrOx@Al2O3 support shows no activity. The presence of FeNi phases increases the conversion of ethane and CO2 marginally (<2%) but forms ethylene at high selectivity (SC2H4 > 80%). The CrOx@Al2O3 support shows some initial activity (XC2H6 < 5%) at very high ethylene selectivity (SC2H4 > 90%) but deactivates with time on stream. Comparison of the ethane and carbon dioxide conversions suggests that direct dehydrogenation rather than the oxidative pathway is taking place. When FeNi particles with the highest Fe content are added, the ethane conversion behavior hardly changes, but the CO2 conversion is increased now supporting the stoichiometric CO2-ODH reaction (SC2H4 > 95%). It is therefore evident that a tandem catalyst system between a reducible oxide carrier and the FeNi species is required. Increasing the Ni content results in an increase in activity and stability while changing the dominant reaction pathway to a combination of dry reforming, CO2-ODH and possibly the reverse Boudouard reaction, with the latter countering catalyst deactivation through carbon deposition.

Promotional effects of Ru and Fe on Ni/ZrO 2 catalyst during CO 2 methanation: A comparative evaluation of the mechanism

Promoting effect of Fe on supported Ni catalysts in CO2 methanation by in situ DRIFTS and DFT study

Single‐Atom Ru Alloyed with Ni Nanoparticles Boosts CO2 Methanation

Iron promoted MOF-derived carbon encapsulated NiFe alloy nanoparticles core-shell catalyst for CO2 methanation

Boosted photothermal synergistic CO 2 methanation over Ru doped Ni/ZrO 2 catalyst: From experimental to DFT studies

Tuning CO2 Hydrogenation Selectivity Via Metal-Oxide Interfacial Sites

Supported FexNiy catalysts for the co-activation of CO2 and small alkanes

RuNi/TiZr-MMO Catalysts Derived from Zr-Modified NiTi-LDH for CO-Selective Methanation

CO2 Methanation over Nickel-Based Catalysts Supported on MCM-41 with in Situ Doping of Zirconium

Screening Transition Metals (mn, Fe, Co, and Cu) Promoted Ni-Based CO2 Methanation Bimetal Catalysts with Advanced Low-Temperature Activities

Ru-based catalysts for efficient CO2 methanation: Synergistic catalysis between oxygen vacancies and basic sites

Effect of Promoters on the Structures and Properties of the RuB/γ-Al2O3 Catalyst

Boosting Low-Temperature CO2 Hydrogenation over Ni-based Catalysts by Tuning Strong Metal-Support Interactions.

Insights into the Zn Promoter for Improvement of Ni/SiO 2 Catalysts Prepared by the Ammonia Evaporation Method toward CO 2 Methanation

Effect of Ru-promotion on the catalytic performance of a cobalt-based Fischer-Tropsch catalyst activated in syngas or H2

Balance effect between Ni dispersion and hydrophobicity in CO 2 methanation over Ni/ZSM-5

Effect of Oxide Support on Catalytic Performance of FeNi‐based Catalysts for CO2‐assisted Oxidative Dehydrogenation of Ethane

Highly Stable and Selective Ni/ZrO 2 Nanofiber Catalysts for Efficient CO 2 Methanation

NiAlFe catalysts based on hydrotalcite-like precursors for low temperature CO 2 methanation: Electronic effects among components and intrinsic activity of Ni site

Ru/MgO catalyst with dual Ru structure sites for efficient CO production from CO 2 hydrogenation

Enhanced Photo‐Thermal CO2 Methanation with Tunable RuxNi1‐x Catalytic Sites: Alloying Beyond Pure Ru