Rationally Tailoring Pore and Surface Properties of Metal–Organic Frameworks for Boosting Adsorption of Dy 3+

Lei Pei,Xudong Zhao,Baosheng Liu,Zhengjie Li,Yinghui Wei

DOI: https://doi.org/10.1021/acsami.1c14302

2021-09-25

Abstract:The adsorption and recovery of dysprosium ions (Dy3+) from industrial wastewater are necessary but still challenging. Herein, we constructed a series of defect-containing metal–organic frameworks (MOFs) [UiO-66-(COOH)2] using sodium benzoate (BCNa) as a modulator. Upon the formation of defects, the porosity and surface charge properties of the MOFs were improved, leading to a higher utilization ratio of active groups and higher adsorption capacities for Dy3+. The synthesized UiO-66-(COOH)2-B10 with an optimal addition of BCNa exhibited a superior adsorption capacity of 150.6 mg g–1. Fast adsorption occurred at ∼5 min, and equilibrium was reached at ∼60 min. Higher pH and temperature were found to be beneficial for boosting Dy3+ adsorption, and selective adsorption over other metal ions was achieved in a multicomponent solution. Further, FTIR spectroscopy and XPS investigations indicate that free carboxyl contributes to the capture of Dy3+. Thus, this work provides a promising strategy to enhance the utilization ratio of active groups and further adsorption performance.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c14302.Schematic diagram of the aperture of the MOF and Dy3+, PXRD pattern of sample B60, N2 adsorption–desorption isotherms at 77 K of sample B60, pore size distributions of the samples based on the DFT method, TG curves of the samples, PXRD pattern of UiO-66-(COOH)2-B10 after three adsorption–desorption cycles, and FTIR spectra of Dy3+-loaded and acid-refreshed UiO-66-(COOH)2-B10 (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology